Polypropylene fiber monofilament form
FUNCTION:
- Resist to shrink & crack
- Increase seepage resistance
- Increase friction resistance
- Increase freezing & thawing resistance
- Improve tendons protection
- Replace steel net (using in plastering)
- Prevent mortar split and crackle expansion
- Increase impact resistance and peeling resistance
FEATURE:
- Easy to be dispersed in mortar or concrete and no agglomeration, it
can guarantee the property of crack resistance effectively
- Easy to be used: No need to change the proportion of mortar, just
put the fibers into the mortar mixture and stir for a moment after
adding water.
- It with fine economic property: The equivalent diameter of PP
monofilament is only φ 0.03mm, so the ratio of diameter and surface
area is high and on the basis of crack resistance, it can reduce
the amount (to about 0.6kg/m 3 ).
- Easy to plaster: As the great number of thin fibers spread into
mortar evenly, the plastering is much easily and this can improve
the binding strength between surface and base.
- It with stable chemical property, strong acid &alkali
resistance, and can be used in any engineering projects.
APPLYING INSTRUCTION:
- Compound Amount. To resist the common cracks on surfaces, 0.6kg/m3
fibers to cement paint is enough, and for reinforced application
0.9-1kg/m3 is enough.
- Stirring requirement. The proportion of cement, sand and aggregate
is no need to be changed. Put cement, aggregate, additive and fiber
together, then stir after adding enough water (Do not stir without
water!) and time for stirring can be prolonged for 2~3 minutes in
order to make the compound mix completely.
SUITABLE PROJECT:
- Be suitable for the water–proof layer, floor, inner &outer wall
of industrial and civil construction.
- Increase cracking resistance on the surface of industrial workshop,
warehouse and parking lot.
- Increase cracking & seepage resistance of the ground in
natatorium, swimming pool, pond and ditch. D). Be suitable for any
mortar projects and fine aggregate concrete projects.
SPECIFICATION:
Raw material | polypropylene |
Crack elongation | 15-20% |
Fiber type | monofilament |
Fiber dia | 18um, 30um |
Melting Point(℃) | 160-170 |
Density(g/cm3) | 0.91 |
Acid &Alkali Resistance | strong |
Tensile Strength (MPa) | 450 Mpa. min. |
Length | 6mm, 12mm, 19mm |
Packing: 1kg per PE bag, 20kg per plastic woven bag. 11500kg in a
20ft.
1kg per PE
bag, 18kg per carton, 450 cartons in a 20ft.
Packing image