1.Description of Alumina ceramic boat
The Ceramic Sagger box offers an all in one solution for firing of either components or powders. These saggers can be stacked directly on top of each other at Temperatures up to 1650 C. Reduced wall thickness over traditional high alumina or mullite refractory saggers can lead to increased product loading, further weight reduction, decreased cycle time.
We product saggars for the application range up to 1750°C. We coordinate the respective saggar type and quality with our customers, depending on the chemical, thermal and geometric requirements. Our long years of experience in manufacturing saggars guarantees long service lives and high-speed heating cycles.
2.Features
1. Refractory, High Temperature Resistance, Maximum Used
Temperature: 1800 ºC (3272ºF)...
2. Hardness Strength Up To Mohs 9.0; HRA 80-90, Wear Resistance
wear rate 0.68 mm3·m-2·h-1
3. High Voltage, Good Insulation Performance ,Electrical
Resistivity Up To 10∧14 Ohm.Cm...
4. High Polished Surface Up To Rz0.8(Ra0.1) ...
5. Superior Mechanical Strength, Max 10 MPa.m1/2 Fracture
toughness,
6. Pressure Resistance, Max 2300MPa compressive strength...
7. Anti-High Corrosion Resistance, Such As Acid Alkali
Resistance...
8. Long Service Life...
9. Other excellent property
item | value |
Place of Origin | China |
Jiangsu | |
Type | Ceramic Plates |
Application | Refractory |
Material | Alumina Ceramic |
Model Number | KT-ALP |
Flexural Strength @ 25 C | 300MPA |
Tensile Strength @ 25 C | 250MPA |
Color | Ivory white |
Raw material | Alumina Powder |
Density | 2.7g/cm3 |
Feature | High temperature resistance |
Thermal Conductivity @ 25 C | 28W / m-Deg K |
Coefficient of Thermal Expansion @ 25-1000 C | 8.1 1 X 10-6 / Deg C |
Shape | FAN SHAPE |
MOQ | 100pcs |
Surface | Polishing Finish |