Lightweight insulating mullite brick white Insulating Refractory fire Brick
1. Description
In mullite (3 2 sio2, al2o3) phase of high aluminum refractory material. General alumina content is between 65% ~ 75%. Mineral composition in addition to the mullite, contain the alumina lower also contains a small amount of glass phase and cristobalite; Containing alumina high contains a small amount of corundum.High refractoriness, can reach more than 1790 ℃. The rul start temperature of 1600 ~ 1700 ℃. Room temperature compressive strength of 70 ~ 260 mpa. Good thermal shock resistance. A sintered mullite bricks and two fused mullite brick.
Sintered mullite brick with high bauxite clinker as the main raw material, add a small amount of clay or raw bauxite as binder, forming, sintering and made. Fused mullite brick with high alumina, alumina industry and refractory clay as raw material, adding charcoal or coke fine as a reducing agent, reduction fused method is used to manufacture after forming.
2. Feature
Mullite insulating bricks characteristics and advantages: 1. Lower content of iron, alkaline and impurities, good high temperature properties. 2. Homogeneous structure, light weight, energy saving because lower heat storage in the furnace during cooling cycles. 3. High strength, good thermal shock resistance under high temperature. 4. Precise sizes due to grinding and shaping after sintering, which meets the requirement of construction. 5. Max service temp: Up to 1730C (3160F)
| Index /brand | 23 | 26 | 28 | 30 | 32 | |
| Classification temperature/ºC | 1260 | 1430 | 1540 | 1650 | 1760 | |
| Bulk density kg/m 3 | 580 | 800 | 950 | 1030 | 1250 | |
| Moudulus of rupture MPa | 0.9 | 1.3 | 1.5 | 1.7 | 2.0 | |
| Cold crushing strength MPa | 1.2 | 1.7 | 2.0 | 2.3 | 3.0 | |
| Permanent Liner Change % C xHr | -0.1 | -0.5 | -0.8 | -0.9 | -0.9 | |
| 1230X24 | 1400x24 | 1510x24 | 1620x24 | 1730x24 | ||
| Thermal expansion coefficient ( 1100 C ) % | 0.45 | 0.50 | 0.55 | 0.60 | 0.65 | |
| Thermal conductivity (W/m.k) | 400 C | 0.17 | 0.24 | 0.30 | 0.40 | 0.49 |
| 600 C | 0.19 | 0.27 | 0.32 | 0.42 | 0.50 | |
| 800 C | 0.22 | 0.30 | 0.35 | 0.44 | 0.51 | |
| 1000 C | 0.25 | 0.32 | 0.38 | 0.45 | 0.53 | |
| 1200 C | 0.35 | 0.39 | 0.47 | 0.55 | ||
| Al2O3 % | 38 | 50 | 64 | 72 | 76 | |
| Fe2O3 % | 0.9 | 0.8 | 0.7 | 0.5 | 0.4 | |
| SiO2 % | 52 | 43 | 33 | 26 | 0.4 | |
| TiO2 % | 1.2 | 1.3 | 0.9 | 0.5 | 0.3 | |
| CaO+ MgO % | 0.7 | 0.6 | 0.4 | 0.3 | 0.2 | |
| K2O+ Na2O % | 1.3 | 1.1 | 0.8 | 0.2 | 0.1 | |
It is mainly used for hot blast stove top, blast furnace and furnace bottom, the regenerator of glass furnace, ceramic sintering kiln, petroleum cracking system corner lining, etc. Also widely used in hot blast stove, metal furnace, ceramic tunnel kilnelectrical porcelain shuttle kiln, etc., has a broad market prospect.
4. Pacakge
Package: The bricks are always palletized and shrink wrapped, usually 1.2~1.5MT per pallet.
Shipping: Delivery by sea or as customer requirment.
Departure Port : Shanghai port or as requirment.