| Item | Specification | Remark | |
| 2.0 Nominal Capacity | 20Ah | 0.5C discharge capacity | |
| 2.1 Minimum Capacity | 20Ah | ||
| 2.2 Internal Impedance | ≤10.0mΩ | By AC 1KHz | |
| 2.3 Nominal Voltage | 3.20V | ||
| 2.4 Cell Weight | 520±10g | containing package | |
| 2.5 End-of-charge Voltage | 3.65V | At CC mode | |
| 2.6 End-of-charge Current | 0.05C | At CV mode | |
| 2.7 End-of-discharge Voltage | 2.00V | ||
| 2.8 Charge Method | 0.5C CC/CV | 180 minutes | |
| 2.9 Quick Charge Method | 1C CC/CV | 90 minutes | |
| 2.10 Max Continuous Discharge current | 40A | Continuous Discharge Time: 30 minutes | |
| 2.11 Max pulse Discharge Current | 60A | Continuous Discharge Time: 10 seconds | |
| 2.12 Cycle Life | ≥2000 cycles | 1C Continual Discharge: ≥80% | |
2.13 Operating | Charging Temperature | 0～45℃ | Ambient temperature:25℃±5℃ |
| Discharging Temperature | -20～55℃ | Ambient temperature: 25℃±5℃ | |
| Storage Temperature | -20～35℃ | Recommended temperature range for long term storage is –10~ +30° | |
| 2.14 Shelf Life | 2 years | ||
| 2.15 Appearance | Without break, scratch, distortion, contamination, leakage and so on | ||
| Test Item | Test Method | Criteria |
| 3.1 55℃ Short- circuit Test | A oven is to be raised to the temperature of 55℃and remain for 10min. A cell is placed into the oven and remain for 30 min~40 min. Then the cell is short-circuited by connecting the positive and negative terminals with copper wire which having a maximum resistance load of 5mΩ. The temperature of cell surface is monitored constantly, until the cell has reached a completely discharged state of less than 0.2 volt or the cell surface temperature has returned to ±10°C (±18°F) than ambient temperature | 1.No fire, no explosion |
3.2 Overcharge | A cell is discharged to cut-off voltage at a constant current of 0.2C, then it is subjected to CC/CV power by connecting its positive and negative terminal, then set the current as 3C, the voltage as 10V, and charging time is not less than 7 hours. | No fire, no explosion |
| 3.3 Forced-Discharge Test | A cell is discharged to cut-off voltage 0V at a constant current of 1C. | No fire, no explosion, no leakage |
| 3.4 Crush Test | A cell is to be placed on the crush flat, the axis is parallel to the crush flat, it is crushed between two flat surfaces. The crushing force is approximately 13 kN and hold for 1min. | No fire, no explosion |
| 3.5 Impact Test | A cell is to be placed on the impact flat. A Φ15.8mm bar is to be placed on the center of the cell. A 9.1kg weight is dropped from a height of 610mm onto the cell, the distortion is allowed. | No fire, no explosion |
3.6 Heating | A cell is heated in a circulating air oven. The temperature of the oven is raised at a rate of 5℃±2℃ per minute to 130℃±2℃ and remain for 30 min before the test is discontinued. | No fire, no explosion |
4. LiFePO4 lithium battery cells 3.2V 20Ah dimension
5. Our Service
6. Certification