ASTM A295 SAE52100 100Cr6 GCr15 EN31 SUJ2 seamless bearing Steel tubes
52100 Bearing Steel Tube:
Process:
Hot rolled:
Steel bar+ Heating+Piercing+Hot rolled+ Cut+ Spheroidize
annealed(optional)+Inspection+Package.
Cold finished:
As shown in the figure below.
Size range:
Outer diameter: Cold finished: 12-219 mm, Hot Rolled: 51mm-530mm
Wall thickness: Cold finished: 1-40mm, Hot Rolled: 5mm-120mm
Length: Not more than 12 m.
| AISI 52100 Chemical Composition | |
| The following table shows the chemical composition of AISI 52100 alloy steel. | |
| Element | Content (%) |
| Iron, Fe | 96.5 - 97.32 |
| Chromium, Cr | 1.30 - 1.60 |
| Carbon, C | 0.980 - 1.10 |
| Manganese, Mn | 0.250 - 0.450 |
| Silicon, Si | 0.150 - 0.300 |
| Sulfur, S | ≤ 0.0250 |
| Phosphorous, P | ≤ 0.0250 |
Equivalent Grades:
| ASTM/ A295 | DIN 17230 | JIS G4805 | BS 970 | GB/T 18254 | ISO 683/17 |
| 52100 | 100Cr6 | SUJ2 | EN31(535A99) | GCr15 | 100Cr6 |
| NF A35-565 | SWEDEN | KS D3525 | TOCT 801 | No. | CNS 3014 |
| 100C6 | SKF3 | STB2 | IIIX15 | 1.3505 | SUJ2 |
Chemical Composition:
| Gcr15 | C | Cr | Si | Mn | P | S | Ni | Cu | Mo |
| Wt% | 0.95-1.05 | 1.40-1.65 | 0.15-0.35 | 0.25-0.45 | ≤0.027 | ≤0.02 | <0.23 | ≤0.25 | ≤0.1 |
| GCr15 | Sn | As | Ti | Sb | Pb | 0 | Al | Ca | |
| Wt% | <0.03 | <0.04 | <0.005 | <0.002 | <0.002 | <0.001 | <0.05 | <0.01 |
AISI 52100 Bearing Steel Bar - Spheroidize Annealed
Introduction:
52100 bearing steels is a high-carbon chromium alloy steel, which,
because of its versatility, is used in a variety of mechanical
applications. In the annealed condition this steel is comparatively
easy to machine, yet very high hardness and abrasion resistance can
be developed by heat treatment to make the steel particularly
suitable for applications requiring extreme wear resistance. In
addition,52100 bearing steels can be heat treated to high levels of
tensile strength and fatigue strength.