[China]
Trade Verify
Address: Room NO.701.702.712. Building 3,Onemall First International,Nancheng District,Dongguan,Guangdong,China.
Contact name:Ariel Zhang
Jiangxi Longtai New Material Co., Ltd |
|
Verified Suppliers
|
|
|
Specialized in the development and sales of all kinds of Cable & Wire Materials,our company is National High-tech Enterprises verified a number of patents and Applicability of Patents.We're professional manufacture for supplying Power Cable PVC Compounds, Instrumentation Cable PVC Compounds, Electric Control Cable PVC Compounds,UL Compounds,Automotive Wire & Cable Compounds, Thermocouple Cables PVC Compounds, Elastomeric Compounds,The Special PVC Compounds,TPE Compounds,Ceranic Flame Retardant & Refractory Compounds for cable Insulation & Inner & Outer Sheath etc.
We will also produce the products according with customer's requirement, For example, Flame retardant compounds, Low temperature resisting compounds, Oil-resistant compounds, and low smoke low halogen compounds, etc.
We have Developed a extensive range of RoHS Compliance PVC Compounds. We have dedicated separate lines to manufacture compounds in compliance with RoHs standards.
1.Technical Specifications
| Test No: SY18170328A | Test Date:Mar 28.2017-Apr.06.2017 | |||
| Sample Name: J1772 | MFG Date: Mar 23,2017 | |||
| Test Reference: UL62&UL2556 | Insulation P/N: Black Jacket | |||
| Item | Requirement | Test Results | Remark | |
| Jacket | Size of Insulator | mm² | 13.86 | T:2.31mm W: 6.0mm |
| Before Ageing | Elongation at Break | > 200% | 410 405 410 | Velocity of the tester 500±25mm/mikn |
| Pull Force | KGF | 12.38 12.49 13.53 | ||
| Tensile Strength | >085KGF/mm² | 0.89 0.90 0.98 | ||
| After Ageing (105 ℃) | Elongation at Break | > % | 425 435 435 | Test Period: 16:00 Mar.29- 16:00 Apr 05 |
| Pull Force | KGF | 14.02 12.63 12.73 | ||
| Tensile Strength | >KGF/mm² | 1.01 0.91 0.92 | ||
| The Remain Elongtaion Rate | > 75% | 104 107 107 | Temperature:136 ℃ Duration:168h | |
| The Remain Tensile Strength Rate | > 75% | 110 99 100 | ||
| Jacket Oil Aging Test | Elongation at Break | > % | 310 320 320 | Test Period: 16:00 Mar.29- 16:00 Apr 05 |
| Pull Force | KGF | 10.34 10.57 10.77 | ||
| Tensile Strength | >KGF/mm² | 0.75 0.76 0.78 | ||
| The Remain Elongtaion Rate | > 75% | 76 78 78 | Temperature:136 ℃ Duration:168h | |
| The Remain Tensile Strength Rate | > 75% | 82 83 85 | ||
| Electrical Performance | Jacket Resistance Test | > 100MΩ | 246.3 GΩ | DC: 500V/1min |
| Physical Performance | Heat Deformation Test | < 50% | 47.6 45.8 46.7 | 150℃ X 1h X 2000g |
| Heat Shock Test | without cracking | without cracking | 150℃ X 1hX Ø34.9mm | |
| Cold Impact Test | Cable Without Cracking | |||
| Cold Bend Test | without cracking | without cracking | ‘- 40℃X 4h X Ø31.8mm | |
| Flammability Test (FT-1) | a. The delay time at every time is not more than 60s after remove flame; b. The bumed area of indication flag on the testing sample is not more than 25% | ok | ||
| Flammability Test (FT-2) | 1.The length of the charred portion of the specimen of cord shall not exceed 100mm not shall flaming particles ignitecotton. 2. Flameless charring of the cotton shall be ignored | < 100mm | ||
| Cable Flexibility Test | Coil 10ft of cable into a cyliner with an inner diameter that is between 260 and 275 mm in diameter (a typical US 5 gal bucket has this diameter) in a single layer with no gaps between the coils. The end of the cable on the top winding is secured to the 2nd turn of the coil. Place the cable and cylinder sample inside a chamber that has been preconditioned to minus -30 ℃ with uncontrolled humidity and leave it for a minimun of 2 hours, Remove the sample from th cylinder and support the top turn of cable at the top of the coil 4 feet above the floor or supporting surface, then allow the other end of the cable to descend under its own weight. Measure the time that it takes for the cable to first touch the floor or supporting surface. Pass/ Fail: if the end of the cable reaches the supporting surface within 2 minutes for the 32 A cable, the criteria is met, 16A cable TBD | Time is 97 seconds cable reaches the supporting surface | ||
2.Use and standard:
3.Process: extrusion
4.Appearance: cylindrical particles, plastication should be good, the color and luster is even, without obvious impurity.
5.color: Black or base on requirement.
Black and white, grey for Shealthing PVC compound
Red, Yellow, Blue, White and black for Insulation PVC compound
6.Packing: 25kg net weight per in a kraft bag,We could support packaging agreed on by both manufacturer and client ! 20 Tons per 20GP, 26 Tons per 40GP
7. Transportation and Storage:
This kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
8.How To order :
1. Let me know the models, specification, quantities, colors you
want to order
2. We will email you the Proforma Invoice based on your order
information
3. Kindly check the PI, everything is ok, we will start production
as soon as receiving payment deposit or LC, then
deliver the goods on request, original documents will be send
against full payment
Any questions, please do not hesitate to contact us.