Flame Retardant ABS Quick Detail:
1.Injection Molding
2.High Flow
3.High Flame Retardant
4.High Impact
Flame Retardant ABS Description:
1. Injection Molding ABS Grade
2. High Flame Retardant: The flame retardant performance of AF312A is excellent. This material is tested based on different thickness. AF312A reached 5VA grade at 2.5mm,5VB grade at 2.0mm, and V0 grade at 1.5mm
3. High Flow: Easy to shape, improve productivity
4. High Impact: High Impact Strength
Flame Retardant ABS Applications:
Electric Parts, IT/OA Device TV, Monitor Housing
Flame Retardant ABS Datasheet:
Properties | Test Condition | Test Method | Unit | Typical Value |
Physical | ||||
Specific Gravity | ASTM D792 | - | 1.19 | |
Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.4~0.7 | |
Melt Flow Rate | 220℃/10kg | ASTM D1238 | g/10min | 60 |
Mechanical | ||||
Tensile Strength, 3.2mm | ASTM D638 | kg/cm2 | ||
@ Yield | 50mm/min | 450 | ||
Tensile Elongation, 3.2mm | ASTM D638 | |||
@ Yield | 50mm/min | % | 5 | |
@ Break | 50mm/min | % | Min 20 | |
Tensile Modulus, 3.2mm | 1mm/min | ASTM D638 | kg/cm2 | 23,000 |
Flexural Strength, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 700 |
Flexural Modulus, 6.4mm | 15mm/min | ASTM D790 | kg/cm2 | 26,000 |
IZOD Impact Strength, 6.4mm | ASTM D256 | |||
(Notched) | 23℃ | kg·cm/cm | 21 | |
-30℃ | kg·cm/cm | 7 | ||
IZOD Impact Strength, 3.2mm | ASTM D256 | |||
(Notched) | 23℃ | kg·cm/cm | 25 | |
-30℃ | kg·cm/cm | 7 | ||
Rockwell Hardness | R-Scale | ASTM D785 | - | 105 |
Thermal | ||||
Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
(Unannealed) | 18.6kg | ℃ | 76 | |
4.6kg | ℃ | 84 | ||
Vicat Softening Temperature | ASTM D1525 | |||
5kg, 50℃/h | ℃ | 83 | ||
1kg, 120℃/h | ℃ | |||
Flammability | UL94 | |||
1.0mm | class | HB | ||
1.5mm | class | V-0 | ||
2.0mm | class | V-0,5VB | ||
2.5mm | class | V-0,5VA | ||
3.0mm | class | V-0,5VA | ||
Relative Temperature Index | UL 746B | |||
Electrical | ℃ | 85 | ||
Mechanical with Impact | ℃ | 75 | ||
Mechanical without Impact | ℃ | 75 |