ABS SG175G Quick Detail:
1. Injection Molding
2. Super Surface Gloss
3. High Melt Flow Index
ABS SG175G Description:
1. Injection molding ABS grade
2. Super Surface Gloss: The surface is very shiny after injection,
usually a colored material such as black.
3. High Melt Flow Index: Easier Injection Molding
ABS SG175G Applications:
Electric/Electronic Products and Miscellaneous Goods(Safety Helmet,
Pipe, Fittings, Vacuum Cleaner, Washing Machine, Toys.)
ABS SG175G Datasheet:
| Properties | Method | Unit | SG175G | |
| Physical | ||||
| Specific Gravity , 23℃ | ASTM D792 | 1.05 | ||
| Mold Shrinkage , 23℃, 3.2mm , 23℃ | ASTM D955 | % | 0.4 ~ 0.7 | |
| Melt Flow Rate , 220℃, 10kg | ASTM D1238 | g/10min | 37 | |
| Mechanical | ||||
| Tensile Strength at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | Mpa | 44 | |
| Tensile Elongation at Yield , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 5 | |
| Tensile Elongation at Break , 23℃, 50mm/min, 3.2mm | ASTM D638 | %, (Min) | 10 | |
| Tensile Modulus , 23℃, 50mm/min, 3.2mm | ASTM D638 | MPa | 2200 | |
| Flexural Strength , 23℃, 15mm/min, 3.2mm | ASTM D790 | Mpa | 71 | |
| Flexural Modulus , 23℃, 15mm/min, 3.2mm | ASTM D790 | MPa | 2500 | |
| Izod Impact Strength , Notched, 3.2mm, 23℃ | ASTM D256 | J/m | 230 | |
| Izod Impact Strength , Notched, 3.2mm, -30℃ | ASTM D256 | J/m | 100 | |
| Izod Impact Strength , Notched, 6.4mm, 23℃ | ASTM D256 | J/m | 220 | |
| Izod Impact Strength , Notched, 6.4mm, -30℃ | ASTM D256 | J/m | 100 | |
| Rockwell Hardness , R-Scale | ASTM D785 | 110 | ||
| Thermal | ||||
| HDT , Edgewise, 1.82MPa, 6.4mm, Unannealed | ASTM D648 | ℃ | 85 | |
| VICAT , 50N, 50℃/h | ASTM D1525 | ℃ | 92 | |
| RTI Electrical | UL 746B | ℃ | 60 | |
| RTI Mechanical with Impact | UL 746B | ℃ | 60 | |
| RTI Mechanical without Impact | UL 746B | ℃ | 60 | |
| Flammability, 1.5mm | UL 94 | HB | ||
| Flammability, 3.0mm | UL 94 | HB | ||