LUPOY PC 1201-08 Injection and Extrusion Molding Grade Plastic Raw Material with FDA Compliance,Medium Viscosity, Good Mold Release Agent and No UV Absorber for Toys, Packaging Applications, Food Utensils
Polycarbonate Quick Detail:
1. Injection and Extrusion Molding Grade
2. FDA Compliance
3. Medium Viscosity
4. Good Mold Release Agent
5. No UV Absorber
Description:
LUPOY PC 1201-08 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
Transparent Polycarbonate Plastic Granules Applications:
Toys, Packaging Applications, Food Utensils.
Datasheet:
| Properties | Method | Value | Units | Value | Units |
| Physical | |||||
| Melt Flow Rate (300 °C /1.2 kg) | ASTM D 1238 | 10 | g/10 min | 10 | g/10 min |
| Density | ASTM D 792 | 1.20 | 1,200 | kg/m3 | |
| Mold Shrinkage | ASTM D 955 | 0.005~0.007 | in/in | 0.005~0.007 | mm/mm |
| Water Absorption @ 24 hrs, 23°C | ASTM D 570 | 0.15 | % | 0.15 | % |
| @ equilibrium, 50%RH, 23°C | ASTM D 570 | 0.32 | % | 0.32 | % |
| Optical | |||||
| Refractive Index, nD | ASTM D 542 | 1.586 | 1.586 | ||
| Light Transmittance | ASTM D 1003 | 89 | % | 89 | % |
| Haze | ASTM D 1003 | 0.7~1.5 | % | 0.7~1.5 | % |
| Thermal | |||||
| Deflection Temperature Under Load (DTUL) @ 4 mm | |||||
| @ 66 psi (0.45 MPa), annealed | ASTM D 648 | 291 | °F | 144 | °C |
| @ 264 psi (1.8 MPa), annealed | 286 | °F | 141 | °C | |
| @ 264 psi (1.8 MPa), unannealed | 262 | °F | 128 | °C | |
| Vicat Softening Point, 50°C /hr, 50N Load | ASTM D 1525 | 300 | °F | 149 | °C |
| Coefficient of Linear Thermal Expansion, @ -40 to 82°C | ASTM D 696 | 38 x 10-6 | in/in/°F | 68 x 10-6 | mm/mm/°C |
| Mechanical | |||||
| Tensile Yield Strength3 | ASTM D 638 | 8,700 | psi | 60 | MPa |
| Ultimate Tensile Strength | ASTM D 638 | 10,300 | psi | 71 | MPa |
| Elongation at Yield | ASTM D 638 | 6 | % | 6 | % |
| Elongation at Break | ASTM D 638 | 150 | % | 150 | % |
| Tensile Modulus | ASTM D 638 | 350,000 | psi | 2,410 | MPa |
| Flexural Strength | ASTM D 790 | 14,000 | psi | 96 | MPa |
| Flexural Modulus | ASTM D 790 | 350,000 | psi | 2,410 | MPa |
| Notched Izod Impact4 @ 23 °C | ASTM D 256 | 17 | ft-lb/in | 900 | J/m |
| Unnotched Izod Impact @ 23 °C | ASTM D 256 | No break | No break | ||
| Instrumented Dart Impact5, Total Energy @ 23 °C | ASTM D 3763 | 770 | in-lb | 87 | J |
| Rockwell Hardness | ASTM D 785 | 118 | R Scale | 73 | M Scale |
| Taber Abrasion Resistance6 (D Haze) | ASTM D 1044 | 45 | % | 45 | % |
| Ignition Resistance7 | |||||
| Limiting Oxygen Index | ASTM D 2863 | 26 | % | 26 | % |
| Ball Indentation Temperature | IEC 598-1 | >125 | °C | >125 | °C |
| Average Extent of Burning | ASTM D 635 | 1 | in | 25 | mm |
| Electrical | |||||
| GWT 2.0 mm, 5 second | IEC 695-2-1 | 850 | °C | 850 | °C |
| Comparative Tracking Index @ 2.0 mm | IEC 112 | 250 | V | 250 | V |
| Dielectric Strength | ASTM D 149 | 420 | V/mil | 17 | KV/mm |
| Dielectric Constant @ 60 Hz | ASTM D 150 | 3 | 3 | ||
| Dissipation Factor @ 60 Hz | ASTM D 150 | 0.001 | 0.001 | ||
| Volume Resistivity @ 23 °C, dry | ASTM D 257 | 2.0 x 1017 | W-cm | 2.0 x 1017 | W-cm |