LUPOY PC 1302-07 Extrusion and Injection Molding Grade Plastic Raw Material with UV Stabilizer, High Viscosity and 0% UV Light Transmittance at Wavelength below 380 nm for Sheet, Optical Lens, Appliances, Film.
Optical Polycarbonate Resin 1302-07 Quick Detail:
1. Extrusion and Injection Molding Grade
2. UV Stabilizer
3. High Viscosity
4. 0% UV Light Transmittance at Wavelength below 380 nm
5. High Impact (at Low Temperature)
Optical Polycarbonate Resin 1302-07 Description:
LUPOY PC 1302-07 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
Optical Polycarbonate Resin 1302-07 Applications:
Sheet, Optical Lens, Appliances, Film.
Optical Polycarbonate Resin 1302-07 Datasheet:
| Properties | Test | English | SI | ||
| Method | Value | Units | Value | Units | |
| Physical | |||||
| Melt Flow Rate (300 °C /1.2 kg) | ASTM D 1238 | 7 | g/10 min | 7 | g/10 min |
| Density | ASTM D 792 | 1.20 | 1,200 | kg/m3 | |
| Mold Shrinkage | ASTM D 955 | 0.005~0.007 | in/in | 0.005~0.007 | mm/mm |
| Water Absorption @ 24 hrs, 23°C | ASTM D 570 | 0.15 | % | 0.15 | % |
| @ equilibrium, 50%RH, 23°C | ASTM D 570 | 0.32 | % | 0.32 | % |
| Optical | |||||
| Refractive Index, nD | ASTM D 542 | 1.586 | 1.586 | ||
| Light Transmittance | ASTM D 1003 | 89 | % | 89 | % |
| Haze | ASTM D 1003 | 0.7~1.5 | % | 0.7~1.5 | % |
| Thermal | |||||
| Deflection Temperature Under Load (DTUL) @ 4 mm | |||||
| @ 66 psi (0.45 MPa), annealed | ASTM D 648 | 293 | °F | 145 | °C |
| @ 264 psi (1.8 MPa), annealed | ASTM D 648 | 288 | °F | 142 | °C |
| @ 264 psi (1.8 MPa), unannealed | ASTM D 648 | 265 | °F | 129 | °C |
| Vicat Softening Point, 50°C /hr, 50N Load | ASTM D 1525 | 304 | °F | 151 | °C |
| Coefficient of Linear Thermal Expansion, @ -40 to 82°C | ASTM D 696 | 38 x 10-6 | in/in/°F | 68 x 10-6 | mm/mm/°C |
| Mechanical | |||||
| Tensile Yield Strength | ASTM D 638 | 8,700 | psi | 60 | MPa |
| Ultimate Tensile Strength | ASTM D 638 | 10,500 | psi | 72 | MPa |
| Elongation at Yield | ASTM D 638 | 6 | % | 6 | % |
| Elongation at Break | ASTM D 638 | 150 | % | 150 | % |
| Tensile Modulus | ASTM D 638 | 350,000 | psi | 2,410 | MPa |
| Flexural Strength | ASTM D 790 | 14,000 | psi | 96 | MPa |
| Flexural Modulus | ASTM D 790 | 350,000 | psi | 2,410 | MPa |
| Notched Izod Impact3 @ 23 °C | ASTM D 256 | 17 | ft-lb/in | 900 | J/m |
| Unnotched Izod Impact @ 23 °C | ASTM D 256 | No break | No break | ||
| Instrumented Dart Impact4, Total Energy @ 23 °C | ASTM D 3763 | 800 | in-lb | 90 | J |
| Rockwell Hardness | ASTM D 785 | 118 | R Scale | 74 | M Scale |
| Taber Abrasion Resistance5 (D Haze) | ASTM D 1044 | 45 | % | 45 | % |
| Ignition Resistance6 | |||||
| UL-94 @ 0.5 mm | ASTM D635 | V-2 | V-2 | ||
| UL-94 @ 1.6 mm | ASTM D635 | V-2 | V-2 | ||
| UL-94 @ 2.5 mm | ASTM D635 | V-2 | V-2 | ||
| UL-94 @ 3.0 mm | ASTM D635 | V-2 | V-2 | ||
| Limiting Oxygen Index | ASTM D 2863 | 26 | % | 26 | % |
| Ball Indentation Temperature | IEC 598-1 | >125 | °C | >125 | °C |
| Average Extent of Burning | ASTM D 635 | 1 | in | 25 | mm |
| Electrical | |||||
| GWT 2.0 mm, 5 second | IEC 695-2-1 | 850 | °C | 850 | °C |
| Compression Tracking Index @ 2.0 mm | IEC 112 | 250 | V | 250 | V |
| Dielectric Strength | ASTM D 149 | 420 | V/mil | 17 | KV/mm |
| Dielectric Constant @ 60 Hz | ASTM D 150 | 3 | 3 | ||
| Dissipation Factor @ 60 Hz | ASTM D 150 | 0.001 | 0.001 | ||
| Volume Resistivity @ 23 °C, dry | ASTM D 257 | 2.0 x 1017 | W-cm | 2.0 x 1017 | W-cm |
Optical Polycarbonate Resin 1302-07 Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
3. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY
AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.