LUPOY PC 1302HP-18 Extrusion Molding Grade Plastic Raw Material with Medium Viscosity, UV stabilizer and Ultra-clean for Diffuser sheet/plate, Appliances, Optical film.
1302HP-18 Quick Detail:
1. Extrusion Molding Grade
2. Medium Viscosity
3. UV stabilizer
4. Ultra-clean
1302HP-18 Description:
LUPOY PC 1302HP-18 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
1302HP-18 Applications:
Diffuser sheet/plate, Appliances, Optical film.
1302HP-18 Datasheet:
| Properties | Method | Value | Units | Value | Units |
| Physical | |||||
| Melt Flow Rate (300 °C /1.2 kg) | ASTM D 1238 | 18 | g/10 min | 18 | g/10 min |
| Density | ASTM D 792 | 1.20 | 1,200 | kg/m3 | |
| Mold Shrinkage | ASTM D 955 | 0.005~0.007 | in/in | 0.005~0.007 | mm/mm |
| Water Absorption @ 24 hrs, 23°C | ASTM D 570 | 0.15 | % | 0.15 | % |
| @ equilibrium, 50%RH, 23°C | ASTM D 570 | 0.32 | % | 0.32 | % |
| Optical | |||||
| Refractive Index, nD | ASTM D 542 | 1.586 | 1.586 | ||
| Light Transmittance | ASTM D 1003 | 89 | % | 89 | % |
| Haze | ASTM D 1003 | 0.7~1.5 | % | 0.7~1.5 | % |
| Thermal | |||||
| Deflection Temperature Under Load (DTUL) @ 4 mm | |||||
| @ 66 psi (0.45 MPa), annealed | ASTM D 648 | 289 | °F | 143 | °C |
| @ 264 psi (1.8 MPa), annealed | ASTM D 648 | 284 | °F | 140 | °C |
| @ 264 psi (1.8 MPa), unannealed | ASTM D 648 | 260 | °F | 127 | °C |
| Vicat Softening Point, 50°C /hr, 50N Load | ASTM D 1525 | 298 | °F | 148 | °C |
| Coefficient of Linear Thermal Expansion, @ -40 to 82°C | ASTM D 696 | 38 x 10-6 | in/in/°F | 68 x 10-6 | mm/mm/°C |
| Mechanical | |||||
| Tensile Yield Strength | ASTM D 638 | 8,700 | psi | 60 | MPa |
| Ultimate Tensile Strength | ASTM D 638 | 9,900 | psi | 69 | MPa |
| Elongation at Yield | ASTM D 638 | 6 | % | 6 | % |
| Elongation at Break | ASTM D 638 | 140 | % | 140 | % |
| Tensile Modulus | ASTM D 638 | 340,000 | psi | 2,340 | MPa |
| Flexural Strength | ASTM D 790 | 14,000 | psi | 96 | MPa |
| Flexural Modulus | ASTM D 790 | 350,000 | psi | 2,410 | MPa |
| Notched Izod Impact3 @ 23 °C | ASTM D 256 | 15 | ft-lb/in | 800 | J/m |
| Unnotched Izod Impact @ 23 °C | ASTM D 256 | No break | No break | ||
| Instrumented Dart Impact4, Total Energy @ 23 °C | ASTM D 3763 | 700 | in-lb | 80 | J |
| Rockwell Hardness | ASTM D 785 | 118 | R Scale | 72 | M Scale |
| Taber Abrasion Resistance5 (D Haze) | ASTM D 1044 | 45 | % | 45 | % |
| Ignition Resistance6 | |||||
| UL-94 @ 0.5 mm | ASTM D635 | V-2 | V-2 | ||
| UL-94 @ 1.6 mm | ASTM D635 | V-2 | V-2 | ||
| UL-94 @ 2.5 mm | ASTM D635 | V-2 | V-2 | ||
| UL-94 @ 3.0 mm | ASTM D635 | V-2 | V-2 | ||
| Limiting Oxygen Index | ASTM D 2863 | 26 | % | 26 | % |
| Ball Indentation Temperature | IEC 598-1 | >125 | °C | >125 | °C |
| Average Extent of Burning | ASTM D 635 | 1 | in | 25 | mm |
| Electrical | |||||
| GWT 2.0 mm, 5 second | IEC 695-2-1 | 850 | °C | 850 | °C |
| Compression Tracking Index @ 2.0 mm | IEC 112 | 250 | V | 250 | V |
| Dielectric Strength | ASTM D 149 | 420 | V/mil | 17 | KV/mm |
| Dielectric Constant @ 60 Hz | ASTM D 150 | 3 | 3 | ||
| Dissipation Factor @ 60 Hz | ASTM D 150 | 0.001 | 0.001 | ||
| Volume Resistivity @ 23 °C, dry | ASTM D 257 | 2.0 x 1017 | W-cm | 2.0 x 1017 | W-cm |