EVER BEST(HK) LIMITED |
|
PC Resin LUPOY 1303EP-22 Extrusion and Injection Molding Grade Plastic Raw Material with Low Viscosity, UV stabilizer and Good Mold Release Agent for Appliances, Automotive headlamps, Outdoor appliances, Mobile Phone Keypads
LUPOY 1303EP-22 Quick Detail:
1. Extrusion and Injection Molding Grade
2. Low Viscosity
3. UV stabilizer
4. Good Mold Release Agent
LUPOY 1303EP-22 Description:
LUPOY PC 1303EP-22 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
LUPOY 1303EP-22 Applications:
Appliances, Automotive headlamps, Outdoor appliances, Mobile Phone Keypads.
LUPOY 1303EP-22 Datasheet:
Properties | |||||
Method | Value | Units | Value | Units | |
Physical | |||||
Melt Flow Rate (300 °C /1.2 kg) | ASTM D 1238 | 22 | g/10 min | 22 | g/10 min |
Density | ASTM D 792 | 1.20 | 1,200 | kg/m3 | |
Mold Shrinkage | ASTM D 955 | 0.005~0.007 | in/in | 0.005~0.007 | mm/mm |
Water Absorption @ 24 hrs, 23°C | ASTM D 570 | 0.15 | % | 0.15 | % |
@ equilibrium, 50%RH, 23°C | ASTM D 570 | 0.32 | % | 0.32 | % |
Optical | |||||
Refractive Index, nD | ASTM D 542 | 1.586 | 1.586 | ||
Light Transmittance | ASTM D 1003 | 89 | % | 89 | % |
Haze | ASTM D 1003 | 0.7~1.5 | % | 0.7~1.5 | % |
Thermal | |||||
Deflection Temperature Under Load (DTUL) @ 4 mm | |||||
@ 66 psi (0.45 MPa), annealed | ASTM D 648 | 288 | °F | 142 | °C |
@ 264 psi (1.8 MPa), annealed | ASTM D 648 | 282 | °F | 139 | °C |
@ 264 psi (1.8 MPa), unannealed | ASTM D 648 | 258 | °F | 126 | °C |
Vicat Softening Point, 50°C /hr, 50N Load | ASTM D 1525 | 297 | °F | 147 | °C |
Coefficient of Linear Thermal Expansion, @ -40 to 82°C | ASTM D 696 | 38 x 10-6 | in/in/°F | 68 x 10-6 | mm/mm/°C |
Mechanical | |||||
Tensile Yield Strength | ASTM D 638 | 8,700 | psi | 60 | MPa |
Ultimate Tensile Strength | ASTM D 638 | 9,500 | psi | 66 | MPa |
Elongation at Yield | ASTM D 638 | 6 | % | 6 | % |
Elongation at Break | ASTM D 638 | 120 | % | 120 | % |
Tensile Modulus | ASTM D 638 | 340,000 | psi | 2,340 | MPa |
Flexural Strength | ASTM D 790 | 14,000 | psi | 96 | MPa |
Flexural Modulus | ASTM D 790 | 350,000 | psi | 2,410 | MPa |
Notched Izod Impact2 @ 23 °C | ASTM D 256 | 14 | ft-lb/in | 750 | J/m |
Unnotched Izod Impact @ 23 °C | ASTM D 256 | No break | No break | ||
Instrumented Dart Impact3, Total Energy @ 23 °C | ASTM D 3763 | 640 | in-lb | 72 | J |
Rockwell Hardness | ASTM D 785 | 118 | R Scale | 72 | M Scale |
Taber Abrasion Resistance4 (D Haze) | ASTM D 1044 | 45 | % | 45 | % |
Ignition Resistance5 | |||||
UL-94 @ 0.5 mm | ASTM D635 | 26 | 26 | ||
UL-94 @ 1.6 mm | ASTM D635 | >125 | >125 | ||
UL-94 @ 2.5 mm | ASTM D635 | 1 | 25 | ||
UL-94 @ 3.0 mm | ASTM D635 | ||||
Limiting Oxygen Index | ASTM D 2863 | 850 | % | 850 | % |
Ball Indentation Temperature | IEC 598-1 | 250 | °C | 250 | °C |
Average Extent of Burning | ASTM D 635 | 420 | in | 17 | mm |
Electrical | 3 | 3 | |||
GWT 2.0 mm, 5 second | IEC 695-2-1 | 0.001 | °C | 0.001 | °C |
Compression Tracking Index @ 2.0 mm | IEC 112 | 2.0 x 1017 | V | 2.0 x 1017 | V |
Dielectric Strength | ASTM D 149 | 0.001 | V/mil | 0.001 | KV/mm |
Dielectric Constant @ 60 Hz | ASTM D 150 | 2.0 x 1017 | 2.0 x 1017 | ||
Dissipation Factor @ 60 Hz | ASTM D 150 | 15 | 15 | ||
Volume Resistivity @ 23 °C, dry | ASTM D 257 | 1.20 | W-cm | 1,200 | W-cm |
LUPOY 1303EP-22 Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. DO NOT INHALE GASEMITTED FROM THE HEATED RESIN.
4. DIRECT CONTACT WITH THE MELTED RESIN MAY CAUSE SEVERE BURNS.
5. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE
PACKAGING BAGS.
6. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY
AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
7. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE
CORRECTLY