PA6 LUMID HI1102A(W) Resin Injection Molding Grade Engineering
Plastic Material with High Impact for H/Lamp Screw Mounting.
LUMID HI1102A(W) Quick Detail:
1. Injection Molding Grade
2. High Impact
3. PA6
LUMID HI1102A(W) Description:
PA6 LUMID HI1102A (W) Resin is designed for Injection Molding. It exhibits an excellent characteristic of High Impact.
LUMID HI1102A(W) Applications:
H/Lamp Screw Mounting.
LUMID HI1102A(W) Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | 23℃ | ASTM D792 | - | 1.1 |
| Molding Shrinkage (Flow), 3.2mm | 23℃ | ASTM D955 | % | 1.2 ~ 1.6 |
| Water Absorption | ASTM D570 | % | 1.4 | |
| Mechanical | ||||
| Tensile Strength, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | kg/cm2 | 600 | |
| Tensile Elongation, 3.2mm | ASTM D638 | |||
| @ Break | 50mm/min | % | > 20 | |
| Flexural Strength, 6.4mm | 2.8mm/min | ASTM D790 | kg/cm2 | 900 |
| Flexural Modulus, 6.4mm | 2.8mm/min | ASTM D790 | kg/cm2 | 22,000 |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 18 | |
| -30℃ | kg·cm/cm | |||
| Thermal | ||||
| Melting Temperature | ASTM D3418 | ℃ | 220 | |
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| 4.6kg | ℃ | 165 |
LUMID HI1102A(W) Caution:
1. THE WORKSHOP FLOOR SHOULD BE KEPT CLEAN AT ALL TIMES IN ORDER TO PREVENT ACCIDENT ASSOCIATED WITH LOOSE PELLETS OR FILM
2. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE PACKAGING BAGS.
3. CARE SHOULD BE TAKEN TO AVOID ACCIDENTS WHEN LOADING, UNLOADING OR STACKING THE PRODUCT.
4. THIS BAG SHOULD NOT BE USED FOR ANY OTHER PURPOSES EXCEPT FOR PACKING THE PELLETS.
5. SOME PHISICAL AND/OR CHEMICAL PROPERTIES OF THIS PRODUCT MAY CHANGE WHEN IT'S MIXED WITH OTHER CHEMICAL PRODUCTS. PLEASE TEST IT AND CONFIRM BEFORE USING IT IN THE CONDITION ABOVE.
FOR MORE INFOMATION ABOUT THE CAUTION, PLEASE CONTACT US.