HIPS Resin 408AF Injection Molding Plastic Raw Material with Flame
Retardant for Electric Parts Requiring Flame Retardant.
HIPS Resin 408AF Quick Detail:
1. Flame Retardant
HIPS Resin 408AF Description:
HIPS Resin 408AF Resin is Designed For Injection Molding, it
exhibits High Flame Retardant for Products.
HIPS Resin 408AF Applications:
Electric Parts Requiring Flame Retardant.
HIPS Resin 408AF Datasheet:
| Properties | Test Condition | Test Method | Unit | Typical Value |
| Physical | ||||
| Specific Gravity | ASTM D792 | - | 1.10 | |
| Molding Shrinkage (Flow), 3.2mm | ASTM D955 | % | 0.4~0.8 | |
| Melt Flow Rate | 200℃/5kg | ASTM D1238 | g/10min | 6.5 |
| Mechanical | ||||
| Tensile Strength, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | kg/cm2 | 270 | |
| Tensile Elongation, 3.2mm | ASTM D638 | |||
| @ Yield | 50mm/min | % | >5 | |
| @ Break | 50mm/min | % | 60 | |
| Flexural Strength, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 400 |
| Flexural Modulus, 3.2mm | 15mm/min | ASTM D790 | kg/cm2 | 22,000 |
| Tear Strength @ Break | 50mm/min | ASTM D624 | kg/cm | |
| IZOD Impact Strength, 6.4mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 9 | |
| -30℃ | kg·cm/cm | 4 | ||
| IZOD Impact Strength, 3.2mm | ASTM D256 | |||
| (Notched) | 23℃ | kg·cm/cm | 13 | |
| -30℃ | kg·cm/cm | 5 | ||
| Rockwell Hardness | R-Scale | ASTM D785 | - | 94 |
| Heat Deflection Temperature, 6.4mm | ASTM D648 | |||
| (Unannealed) | 18.6kg | ℃ | 81 | |
| 4.6kg | ℃ | 87 | ||
| Vicat Softening Temperature | ASTM D1525 | |||
| 5kg, 50℃/h | ℃ | 84 | ||
| Flammability | UL94 | |||
| 0.8mm | class | V-2 | ||
| 3.0mm | class | V-2 | ||
| Relative Temperature Index | UL 746B | |||
| Electrical | ℃ | 50 | ||
| Mechanical with Impact | ℃ | 50 | ||
| Mechanical without Impact | ℃ | 50 |
HIPS Resin 408AF Caution:
1. AVOID DIRECT SUNLIGHT, STORE IN COOL, DRY VENTILATED AREA.
2. KEEP AWAY FROM THE HEAT, SPARK, AND FLAME.
3. ENSURE THE PELLETS AND PACKAGING BAGS ARE DISPOSED OF PROPERLY
AND IN COMPLIANCE WITH LOCAL/STATE REGULATION.
4. LIFTING OF HEAVY BAGS CAN CAUSE DAMAGE TO YOUR SPINE IF NOT DONE
CORRECTLY.
5. DO NOT EAT THE PELLETS AND AVOID INHALING DUST PARTICLES IN THE
PACKAGING BAGS.
FOR MORE INFOMATION, PLEASE CONTACT US.