Rigid Self-leveling Polyaspartic Flooring Coating & Film Feature Testing
Part I * Technical Data
No. | Item | Result | |
1 | Solid content % | 97 | |
2 | Fineness,um | 30 | |
3 | Pot life,min | 35 | |
4 | Dry time/h | Touch dry | 42min |
Hard dry | 24h | ||
6 | Tensile strength,MPa | 40 | |
7 | Elongation at break,% | 9% | |
| Hardness(Shore D) | 75 | |
8 | Flexibility at low temp(-20℃),mm | 6cm | |
| Abrasion Resistance (1KG/1000,mg) | 21mg | |
* Gloss Stablility Testing
After Mix | 0 min | 5 min | 10min | 15min | 20min | 25min | 30min |
Final gloss | 92 | 92 | 91.5 | 92 | 91.5 | 91.5 | 91.5 |
Part II * Component A (Paint)
Material Name | Content (%) |
F420 Polyaspatic Resin | 25 |
F520 Polyaspartic White plasm | 26 |
F520 Polyaspartic Resin | 18 |
F524 A3 Polyaspartic A3 plasm | 12 |
F524 Polyaspartic Resin | 15 |
H15 Dustproof Agent | 0.3 |
BD8330 Dispersant | 0.2 |
2722 Anti-foam Agemt | 0.8 |
3600 Leveling Agent | 0.2 |
KH560 Coupling Agent | 2.5 |
* Component B (Hardener)
Material Name | Content (%) |
N3390 | 70 |
HMDI | 20 |
GB905-85 | 10 |
* Ratio A:B=1:0.5