| ITEM | Standard | UNIT | Data | |
| Adhesive | softening point | ASTM E 28 | °C | 70-80 |
| shear strength | DIN 30 672 | N/cm | ≥100 | |
| Basic | specific density | ASTM D792 | r/cm 3 | 0.935-0.96 |
| tensile strength | ASTM D638 | Mpa | 15-20 | |
| Elongation at break | ASTM D792 | % | 350 | |
| hardness | ASTM D2240 | ball | 48 | |
| Heat Shrinkable Sleeve | peel strength | ASTM D1000 | N/cm | >150 |
| water-intake rate | ASTM D570 | % | 0.05 |
Move the heat shrink sleeve to the centered position at the joint
and take out the isolation material. Heat evenly from the center
along the circumference, make it shrink completely and then extend
the heating to both ends respectively. Pay attention to the even
fire. After all the shrinkage is completed, reheat the uneven
surface to make it completely flat. After the overall heating is
completed, turn down the flame and reheat again to make the hot
melt adhesive fully overflow. During the heating process, use the
pressure roller to roll the joint several times, focusing on
rolling the fusion lap to eliminate air bubbles.
Feature
1.Fast shrinkage speed,
2.good waterproof performance,
3 good anti-corrosive performance,
4.long service life, convenient transportation and fast
construction.
2. 3Layer Fiber
reinforced PE heat shrinkable tape (sleeve) is composed of
cross-linked polyethylene back, a middle layer of fiber and special
heat melt adhesive an. The 3 layer reinforced sleeve gives better
shrink ratio, and better strength. It is resistant to corrosion,
wear, impact, UV and aging, easier to be operated.
Application area:
It is mainly used for Hollow wall spiral pipe, corrugated pipe and
metal reinforced corrugated spiral pipe etc.
TEST PROCEDURE
1. Clean the steel pipe and heat it by fire till over 80 ºC
2. Paint the steel pipe with Primer (mixed with A&B)
3. Fire heat the heat shrink sleeve, be attention to start heating
from middle of the sleeve, but act from up and down, and gradually
move from middle to two sides of sleeve, in order to drive air out
of the sleeve, after finish heating, the good result is that there
is about 1-2mm hot adhesive melt at the edge of sleeve.
TEST RESULT
1. Test result after cooling about 40 minutes.
Peel strength to primer is over 100N per 2cm(till the end of the
spring balance). at 30.7ºC
Co-adhesive: Half-half.
2. Test result after cooling about 24hours.
Peel strength to primer is over 172N per 2cm at room temperature
about 30.7ºC
Co-adhesive: Half-half.
3. 2. Test result after cooling about 24hours.
Peel strength to primer is over 9.2kg/90N per 1cm at room
temperature about 30.7ºC
Co-adhesive: Half-half.