Natural Heat Resistant Nylon PA6 Glass Fiber Reinforced Plastic

Active Member

Contact Us

[China]

Address: 1-1 No.600,TongJiang Zhong Road,ChangZhou,JiangSu,china

Contact name:gong

ChangZhou Polisen Plastics Technology Co., Ltd.

Natural Heat Resistant Nylon PA6 Glass Fiber Reinforced Plastic

Country/Region china
City & Province changzhou jiangsu

Product Details

 

 

Specifications:

 

It can be customized high rigidity, high toughness and a variety of heat-resistant glass fiber content of the material according to customer requirements, and can choose a variety of colors.

 

 

Description:

 

Trademark

01010G

01020G

01030G

01040G

Item

Unit

Test Methods

GF10

GF20

GF30

GF40

      Performance

 

Density

g/cm3

ISO 1183

1.18

1.27

1.36

1.45

Glass fiber content

%

ISO 3451-4

10± 1

20± 1.5

30± 2

40± 2

Melt Index 230/2.16

g/10min

ISO 1133

15±1

12±1

10±1

8±1

Moisture content

%

 

≤ 0.5

≤ 0.5

≤ 0.5

≤ 0.5

Shrinkage   

%

ISO 294-4

0.5-1.0

0.4-0.8

0.35-0.7

0.3-0.5

Mechanical behavior

 

 

 

 

 

 

Tensile Strength

MPa

ISO 527

105

115

150

170

Elongation at break

%

ISO 527

5

4

4

3

Bending strength

MPa

ISO 178

160

175

190

210

Bending modulus

MPa

ISO 178

4600

5500

7800

9000

Charpy notched impact strength

KJ/m2

ISO 179

8

12

16

18

Charpy impact strength

KJ/m2

  ISO 179

40

60

80

88

Thermal Properties

 

 

 

 

 

 

Heat distortion temperature /1.8 MPa

ISO 75-2

160

190

210

210

Heat distortion temperature /0.45 MPa

 

 

200

200

210

215

Melting point

ISO 3146

215

215

215

215

Combustion performance  3.2mm

class

UL94

HB

HB

HB

HB

Short-term maximum operating temperature

 

200

200

200

200

Electrical Properties

 

 

 

 

 

 

Permittivity  1MHz

 

IEC 60250

3.5

3.6

3.6

3.7

Permittivity

KV/mm

IEC 60243

23

24

24

27

Surface resistivity

Ω

IEC 60093

1012

1012

1012

1013

Volume resistivity

Ω.m

IEC 60093

1013

1013

1012

1013

Tracking Index CTI

 

IEC 60112

CTI 550

CTI 550

CTI 550

CTI 550

 

Note: The above data is sample preparation material after drying for 24 hours at 23 ℃, 50% humidity measured.

 

 

product manual:

 

DriedDrying

Temperature

100-120

Time

H

4-5

 

Molding

Temperature

Nozzle

245±10

Second District

235±10

Third District

230±10

Four districts

210±10

Mould Temp

70-90

Pressure

Mpa

70-95

  Molding Speed

%

70-100

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Remark:

According to the injection molding method of injection molding conditions and mold die structure is different, to do the appropriate adjustments.

 

 

Advantage:

 

Low fiber content

Moderate rigidity

Good toughness products look good

Medium glass content, good mechanical properties and dimensional stability

High rigidity, good dimensional stability and heat resistance

High rigidity, high strength, excellent dimensional stability and wear resistance

Hot Products

Specifications: polyamide (nylon)6 with excellent molding characteristics . Super tough, high ...
Specifications: Nylon PA6 Pellets: High softening temperature, heat resistance Wear-resistance, self...
Specifications: It can be customized high rigidity, high toughness and a variety of heat-resistant ...
Specifications: Modified nylon generally used nylon resin chips viscosity of about 2.7 Because this ...
Specifications: Modified nylon 6 products, full range, can be customized flame retardant, reinforced...
Specifications: Universal grade nylon 6 material, widely used in injection molding, modified binder, ...