TZM Molybdenum Alloy Top Head
1.Product Descriptionn of TZM Molybdenum Alloy Top Head:
The mandrel head for the seamless steel pipe is constructed from a molybdenum alloy called the molybdenum top head, which is composed of molybdenum, titanium, zirconium, and carbon. For seamless perforated steel pipes made of materials including molybdenum, molybdenum alloy, stainless steel, brazing steel, and other specialty parts.
The basic material for the top head of the molybdenum alloy is molybdenum powder FMo-1 mixed with rare earth material. This material is then processed by mixing, forming, shaping, high temperature sintering, and other steps to create the finished product. The final item has a density of around 9.4g/cm3.
2.Product size of TZM Molybdenum Alloy Top Head:
| Type | Diameter | Tolerance of diameter | Length | Tolerance of length |
DM20 DM25 DM30 DM35 DM40 | 20mm 25mm 30mm 35mm 40mm | 0~+3mm | 60~80mm | 0~+6mm |
DM45 DM50 DM55 | 45mm 50mm 55mm | 0~+3mm | 80~110mm | 0~+6mm |
DM60 DM62 DM64 DM66 DM68 DM70 DM72 DM74 DM76 DM78 DM80 | 60mm 62mm 64mm 66mm 68mm 70mm 72mm 74mm 76mm 78mm 80mm | 0~+4mm | 160~200mm | 0~+8mm |
DM85 DM90 DM95 DM100 | 85mm 90mm 95mm 100mm | 0~+6mm | 180~260mm | 0~+8mm |
DM110 DM120 DM130 DM140 DM150 | 110mm 120mm 130mm 140mm 150mm | 0~+8mm | 200~300mm | 0~+10mm |
3.The TZM Molybdenum Alloy Top Head Manufacturing Process:
Molybdenum powder→preparation of additives→mixing of molybdenum powder and additives→pack material→cold isostatic pressing→turning and repairing→high temperature sintering in intermediate frequency furnace→inspection→finished product
4.Characteristic of TZM Molybdenum Alloy Top Head:
High temperature strength, good high temperature oxidation resistance, long service life, corrosion resistance and not easy to color glass.
5.Application of TZM Molybdenum Alloy Top Head:
For seamless perforated steel pipes made of materials including molybdenum, molybdenum alloy, stainless steel, brazing steel, and other specialty parts. It is mainly used for the perforation of seamless steel pipes such as stainless steel, brazing steel, bearing steel and high-temperature alloy steel, and for the severe, high-temperature hot-rolled perforation of seamless pipes made of various materials.