Aluminium Extrusion Mould Forged 1.2714 Tool Steel Block

Country/Region	china
City & Province	dongguan guangdong
Categories	Moulds

Product Details

Forged Production 1.2714 Tool Steel Block For Aluminium Extrusion Mould

Steel Grade: Hot Work Tool Steel
Standard: AISI, ASTM, BS, DIN, GB, JIS
Dimensions: 20~800MM
Place of Origin: China (Mainland)
Brand Name: songshun
Model Number: DIN 1.2714
Technique: Forged
Application: Tool Steel Bar
Alloy Or Not: Is Alloy
Special Use: Mold Steel
Type: Alloy Steel Bar
Mould name: Songshun din 1.2714 steel of good price 1.2714
Shape: Round bars/Flat bar/Plate
Technology: Hot Rolled/Forged/Clod Drawn
Heat treatment: Annealing/Q+T
Surface treatment:Black/Peeling/Polishing/Machined
Delivery condition: Hot rolled or forged/ Peeled or black surface/annealed or QT
Test: SGS/UT100%/Elements testing
Certificate: ISO/Mill certificate
Service: Sample free and 24 hours online
Experience: Ten years manufacturer experience

1.2714 steel Packaging & Delivery

Packaging Details:	seaworthy packing; 20ft: GW:17.5T; (5.80mX2.13mX2.18m,) 40ft: GW:22T; (11.8mX2.13mX2.18m,)
Delivery Detail:	4~7 days after the order is confirmed

Hot work steel 1.2714 Specifications

Songshun din 1.2714 steel of good price 1.2714
1.A/N/Q+T provide
2.Sample free
3.Black or Bright
4.D: Max:800mm

1.2714 steel Product Description

Songshun din 1.2714 steel of good price 1.2714

1.Specifications of din 1.2714 steel of good price 1.2714

Round bar

Diameter(mm)

Length (mm)

20~800

3000~5800

Plate

Thickness(mm)

Width (mm)

Length (mm)

Max:800

205~810

2000~4000

The size can be customed

2.Chemical composition(%) of din 1.2714 steel of good price 1.2714

0.50- 0.60

0.10- 0.40

0.65- 0.95

1.00- 1.20

0.45-0.55

0.07-0.12

1.50-1.80

0.03max

Similar standards

AISI/SAE

DIN

W.Nr.

JIS

GB,YB

6F2

56NiCrMoV7

1.2713

1.2714

SKD4

SCrNiMo

3.Heat treatment of din 1.2714 steel of good price 1.2714

Isothermal annealing:

-Heat to 800°Cand hold at temperature for 1/2 h to 1 h;

-Furnace cooling to 670°Cand hold at temperature for at least 10 hours;

-Cool by 10°C/h to 630°C;

-Cooling in air.

Maximum hardness:≤240 HB

Stress relieving:

To be carried out after maching before the final heat treatment.

-Heat to 600-650°C, hold for 4-6 hours;

-Cooling in furnace to 300-350°C;

-Cooling in air

Hardening:

-Initial preheating to 350-450°C;

-Second preheating to 650-750°C;

-Heat to hardening temperature 860-890°Cand hold at temperature;

-Cooling in hot oil (40-60°C); Tempering hardness: 45~45HRC

Tempering:

Tempering must be carried out within one hour from hardening(warm part)

in the range 550-630°Cfor 4-6 hours according to hardness required, the

dimensions of the parts and operating conditions.