Sae 52100 Bearing Alloy Steel Round Bar Cold Worked High Hardened 62-66 HRC

SAE 52100 cold worked hardened alloy steel round bar

SAE 52100 Steel is a steel high carbon content, linked to chromium, used for processing when you want to achieve high hardness after hardening, between 62-66 HRC. It is a hardenable steel in oil.

Chemical Composition – C (0.98 – 1.10), Si (0.15-0.35), Mn (0.25-0.45), Cr (1.30-1.60)

Supply conditions – Supplied with maximum hardness of 250HB

APPLICATIONS

It is generally used components in the bearing manufacturing industry.

FORGING

ANSI 52100 steel should be held at a minimum temperature of 925 ºC and a maximum of 1150 ºC.

HEAT TREATMENT

Annealing: For its high carbon content of the steel 52100 must undergo spheroidizing annealing to optimize its machinability. The spheroidization is performed at around 750 ° C for times ranging between 15 and 20 hours. Cool the oven.

Standardization: The treatment should be done at the temperature of 870 – 890ºC for at least 1 hour for every 25 mm. Cool air. In special cases can use forced air.

Hardening: The austenitizing tempering must be carried out between 840 – 850 ° C, maintaining the time necessary to homogenize the temperature in cross section and cooling in oil.

Tempering: It must be done immediately after hardening when the temperature reaches about 70 ° C. The tempering is performed at temperatures between 120 – 200 ° C. The usual tempering temperature is around 150 ° C. Under these conditions there is no significant drop in hardness. In tempering at about 180 ° C the hardness can fall of 1 to 2 points HRC. The hardness variation as a function of the tempering temperature curve is shown in Arrangement below.

Product size range

Diameter: 40mm - 150mm

Length: on request

Production Process

Key clients