Factory Ferro Nickel Alloy Invar 36 4J36 Nickel Plate Price Hot Rolled Sheet
1 . Description
Invar (also know as Invar 36, NILO 36, Pernifer 36, and Invar Steel) is a low expansion alloy consisting of 36% Nickel, balance Iron. Invar Alloy exhibits extremely low expansion around ambient temperatures, making Invar Alloy particularly useful in applications where minimum thermal expansion and high dimensional stability is required, such as in precision instruments like optoelectronic devices, optical and laser benches, electronics, and other kinds of scientific instruments.
Product Name | Factory Ferro Nickel Alloy Invar 36 4J36 Nickel Plate Price Hot
Rolled Sheet |
Standard | ASTM, AISI, GB, JIS, EN, DIN |
Specification | Width: 500~1500mm |
Thickness: 0.2~8.0mm | |
Thickness: 0.2~8.0mm | |
Type | Cold/Hot rolled plate, thick plate, color coated plate, galvanized
plate |
Material | 200 series: 201, 202 300 series: 301, 302, 303, 304, 304L, 309, 310, 310S, 316, 316L, 321, 347 400 series: 409, 410, 420, 430, 440 600 series: 15-5PH, 17-4PH, 17-7PHOther: 9004L Duplex: 254SMO, 2205, 2507, ASTM A694, S32760 Hastelloy: B/B-2/B-3/C-4/C-22/C-276/C-2000/G-30/G-35/X/N; Haynes: 230/556/188 Inconel: 600/601/617/625/686/690/718/725/783/X-750 Incoloy: 800/800H/800HT/825/925/926/A-286 GH: GH2132, GH3030, GH3039, GH3128, GH4180, GH3044 Monel: 400/K500 Nitronic: 40/50/60 Nimonic: 75/80A/90 |
Quality | MTC |
Package | Standard seaworthy package or Customized. |
Delivery Time | 5-30 working days after receiving the down payment. |
*Payment Term | Trade assurance, By T/T, 50% down payment, 50% balance before shipment. |
2 . Typical Physical Properties
| Density (g/cm3) | 8.1 |
| Electrical resistivity at 20℃(Ωmm2/m) | 0.78 |
| Temperature factor of resistivity(20℃~200℃)X10-6/℃ | 3.7~3.9 |
| Thermal conductivity, λ/ W/(m*℃) | 11 |
| Curie point Tc/ ℃ | 230 |
| Elastic Modulus, E/ Gpa | 144 |
3 . The Heat Treatment Process
The heat treatment process | |
Annealing for stress relief | Heated to 530~550℃ and hold 1~2 h. Cold down |
annealing | In order to eliminate hardening, which be bring out in cold-rolled, cold drawing process. Annealing needs heated to 830~880℃ in vacuum,hold 30 min. |
The stabilization process | 1) In protective media and heated to 830 ℃, hold 20min. ~ 1h, quench 2) Due to the stress generated by quenching, heated to 315℃,hold 1~4h. |
Precautions | 1) Can not be hardened by heat treatment 2) Surface treatment can be sandblasting, polishing or pickling. 3) Alloy can be used 25% hydrochloric acid pickling solution at 70 ℃ to clear oxidized surface |