E71T-1C Flux Cored Arc Welding Wire 0.045 / 0.052 / 0.0625 (1/16) In. 2/11/33/44 lb
LT·E711 Conform to Standard :
GB/T 10045 E501T-1
AWS A5.36 E71T-1C
JIS Z3313 E492T1-1CA
ISO 17632-B-T492T1-1CA
Specification:
E71T-1C
E71T-1C is a flux cored wire designed for single or multi pass welding having a smooth arc transfer, low spatter, flat to slightly convex bead contour, with a high deposition rate and easily removal slag. This all-position wire has excellent feeding and low fume generation using 100% CO2 making it a good choice for mild steel and higher strengths steels. Argon - CO2 gases may be used if tested with application.
Purpose:
Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery
Chemical Composition(%)(Shielding Gas:CO2)
| Chemical Composition | C | Mn | Si | S | P |
| Guarantee Value | ≤0.18 | ≤1.75 | ≤0.90 | ≤0.030 | ≤0.030 |
| General Result | 0.05 | 1.28 | 0.39 | 0.010 | 0.016 |
Mechanical Properties of Deposited Metal(Shielding Gas:CO2)
| Test Item | Rm(MPa) | ReL/Rp0.2(MPa) | A(%) | KV2(J) |
| -20℃ | ||||
| Guarantee Value | ≥480 | ≥400 | ≥22 | ≥27 |
| General Result | 550 | 470 | 27 | 115 |
Diffusion hydrogen content of the deposited metal (Mercury Method):≤10ml/100g
X-Ray Radiographic Test Requirements:Grade II
Reference Current(DC+)
| Size(mm) | Φ1.2 | Φ1.4 | Φ1.6 | |
| Current Range (A) | Flat Position | 120~300 | 150~400 | 180~450 |
| Vertical Upward welding/ Overhead position | 120~260 | 150~270 | 180~280 | |
| Vertical Downward weldingOverhead position | 200~300 | 220~300 | 250~300 | |
| Horizontal Welding | 120~280 | 150~320 | 180~350 | |
Notes:
1.Adopt degreasing and rust cleaning process before operate.
2.Shielding gas flow: 20-25L/min when welding
3.Extension: 15-25mm
4.The humidity of welding wire storage should be less than 60%
5.Storage period: Vacuum packaging less than 1 Year, other packaging less than half year.