Magnesium Insulation Brick Mgo-C Fire-Resistant Bricks With High Quality
Product information
Magnesite brick using density sintered magnesia as raw material, it has high refractoriness,resistance to erosion ability, load soft higher characteristic, suitable for titanium slagfurnace molten pool and furnace wall slag line work layer.
Shapes &Sizes of our magnesium oxide bricks
| Straight | Split | Arch | Wedge | Tile | Other Shape |
| L×W×H(mm) 230×114×65 230×114×75 | L×W×H (mm) 230×114×25 230×114×32 230×114×37 230×114×50 | L×W×H/h(mm) 230×114×65/45 230×114×65/55 230×114×75/45 230×114×75/55 230×114×75/65 | L×W×H/h (mm) 230×114×65/45 230×114×65/55 220×114×75/45 220×114×75/55 220×114×75/65 | L×W×H (mm) 230×230×38 230×230×50 230×230×65 230×230×75 | Key brick, Skew brick, Soap, Checker, Neck, Taper, |
Physical and chemical indexes
| Item | MZ-97 | MZ-95 | MZ-93 | MZ-91 |
| MgO % | ≥97 | ≥95 | ≥93 | ≥91 |
| SiO2 % | ≤1.0 | ≤2.0 | ≤3.5 | - |
| CaO % | - | ≤2.0 | ≤2.0 | ≤3.0 |
| Apparent porosity/% | ≤16 | ≤16 | ≤18 | ≤18 |
| Cold crushing strength/ Mpa | ≥60 | ≥60 | ≥60 | ≥60 |
| Refractoriness under load, 0.2MPa, °C | ≥1700 | ≥1650 | ≥1620 | ≥1560 |
| Reheating Linear Change(1650 °C,2h) /% | 0~-0.2 | 0~-0.3 | 0~-0.4 | 0~-0.4 |
Feature of Our refractory magnesia bricks
1. High refractoriness,usually the refractoriness is above 2000°C.
2. Refractoriness under load about 1500-1550°C because of poor high-temperature intensity.
3. Strong ability to resist basic (alkaline) slag,can not contact with acid refractory material.
4. Poor Thermal shock resistance,so keep the temperature of furnace stabilized.
5. Poor Volume stability at high temperature,must set aside appropriate expansion joint when laying brick.
6. Strong ability of thermal conductivity,sometime need insulating material.
7. Hydrability, keep product away from moisture during storage.
Applications of our refractory magnesia bricks
1. Iron Steel Industry
steelmaking furnace lining, ferroalloy furnace, metal mixer furnace lining, converter lining, arc furnace wall and furnace bottom, soaking furnace, heating furnace bottom
2. Non-ferrous metallurgical industry
copper,nickel,lead,zinc,tin smelting furnace lining, refined copper reverberatory furnace,ore electric furnace lining
3. Glass Industry
glass furnace regenerator checker
4. Building Material Industry
lime kiln,cement kiln
5. Refractory Material Industry
High temperature calcination kiln,shaft kiln and tunnel kiln