Magnesia Chrome Bricks are made from high grade magnesite clinker and chrome oxide. By high pressure shaping and high temperature firing, its characteristic is the high direct-bonding rate, and big crystallite. It has a good thermal spalling resistance. The low-basic neutral nature gives itself a good slag resistance when servicing low-acid feed furnaces. The bricks is a realistic lining material for refining furnace, electric furnace, glass melting furnace and cement rotary kiln etc.
Specification
Item | Chrome Magnesite Brick | |||||||
Mg-Cr-6 | Mg-Cr-8 | Mg-Cr-9 | Mg-Cr-12 | Mg-Cr-16 | Mg-Cr-18 | |||
Chemical Content | MgO | ≥86 | ≥84 | ≥83 | ≥80 | ≥76 | ≥74 | |
Cr2O3 | ≥6 | ≥8 | ≥9 | ≥12 | ≥16 | ≥18 | ||
SiO3 | ≤1.8 | ≤1.8 | ≤1.8 | ≤2.5 | ≤2.8 | ≤2.8 | ||
Bulk Density, g/cm3 | ≥2.90 | ≥2.95 | ≥3.0 | ≥3.0 | ≥3.05 | ≥3.10 | ||
Apparent porosity ,% | ≤18 | ≤17 | ≤17 | ≤17 | ≤17 | ≤17 | ||
Cold Crushing Strength, Mpa | ≥50 | ≥50 | ≥50 | ≥50 | ≥45 | ≥45 | ||
Refractoriness, ℃ | T0.6 | ≥1600 | ≥1650 | ≥1700 | ≥1700 | ≥1700 | ≥1700 | |
Thermal shock resistance (1100℃ water), time | ≥4 | ≥5 | ≥7 | ≥7 | ≥7 | ≥7 | ||
Performance | High temperature structure with high intensity, high refractoriness under load, strong resistance to chemical attack, etc. | |||||||
Application | Widely used in cement rotary kiln calcining zone, glass furnace, steel-making furnace, converter, as well as the melting furnace of non-ferrous metal. | |||||||