0.8mm Thickness High Strength PU Coated Glass Fabric For Fabric Expansion Joint
1. Description:
This PU-coated glass fiber is made of glass fiber fabric with a double-sided polyurethane coating. It can withstand temperatures up to 260°C. This type of fiberglass cloth is a medium-weight cloth (800gsm fiberglass cloth) with a specially formulated polyurethane coating. PU-coated glass fiber fabric has very good abrasion resistance and good oil resistance and solvent resistance. It has good mechanical properties and is very suitable for further processing. This kind of fireproof PU-coated glass fiber cloth has a wide range of applications in fabric expansion joints, fire curtains, smoke screens, fire barriers, heat insulation fabrics, and other types of smoke prevention and fire protection systems. The heat-insulating glass fiber fabric is coated with a polyurethane coating, which increases the non-slip and waterproof performance. PU-coated glass fiber cloth is an economical lightweight thermal insulation or fire-resistant thermal insulation fabric. We produce single-sided/double-sided polyurethane-coated glass fiber cloth, which can be customized in different colors and widths
Specification: 3784 Double-sided Pu Coated Fiberglass Fabric
Treatment: Double sides Pu Coating
Total Thickness: 0.8mm
Contact Warp & Weft: 100% fiberglass yarns
Weight: 26.7 oz/yd2
Weave Structure: Satin Weave
Width: 100cm, 120cm and Customized
Thread Count: Warp 47.5/inch, Weft 25/Inch
Temperature Resistance: It withstands temperatures up to 180℃, and 550℃ for short bursts.
2. Table 1: TDS for Basic Cloth
| 3784 | ||
| Item Model | 3784 Fiberglass Fabric | |
| Description | Woven Fiberglass Cloth | |
| Weave Structure | 8H Satin Weave | |
| Weight | 850gsm | |
| Thickness | 0.8mm | |
| Yarn Type | Warp | EC9 33 4*2 |
| Weft | EC9 33 4*2 | |
| Thread Count | Warp | 18±1 ends/cm |
| Weft | 14±1 picks/cm | |
| Break Strength | Warp | 7500 N/5cm |
| Weft | 5600 N/5cm | |
| LOI | < 0.4% | |
| Working Temperature | ≤550℃ | |
3. Table 2: Pu Coated Fiberglass Cloth Information
| Item | 3784 Fiberglass Fabric with Double-sided Pu Coating |
| Total Weight | 850 g/m2 |
| Thickness | 0.8 mm |
| Color | Grey Silver White (Other colors need to be customized) |
| Working Temperature | Glass fabric up to 5500C Polyurethane coating up to 2600C |
| Coating | Fire retardant, high performance, blue/black polyurethane on both sides |
| Width | 100,120,150,200cm |
4. Properties:
Good strength and wear resistance
Lightweight, easy to cut and manufacture
Good flame retardant and fireproof
Waterproof, chemical, and oil resistant
Color can be made as required
5. Application:
Thermal insulation jacket, mattress, and pad
Expansion joints and compensators
6. Much More Choice for PU coating:
This kind of raw material is normally used on welding & fire protection, thermal insulation jackets, mattress, expansion joint belt, a protective scrim of insulation wool, composite reinforcement
| Type | Thickness | Weight | ||
| mm | inch | g/m2 | oz/yd2 | |
| 3732 with Double-sided Pu Coating | 0.5 | 0.0197 | 460±20 | 13.6 |
| 3732 with Double-sided Silicone Coating | 0.5 | 0.0197 | 540±20 | 15.9 |
| 3734 with Double-sided Pu Coating | 0.5+ | 0.02 | 510±20 | 15.04 |
| 3734 with Double-sided Silicone Coating | 0.5+ | 0.02 | 590±20 | 17.4 |
| Stainless Steel Wire Insert Fiberglass cloth with Double-sided Pu Coating | 0.6 | 0.0236 | 700±20 | 21 |
| 3784 with Double-sided Pu Coating | 0.8 | 0.0315 | 890±30 | 26.7 |
| 3784 with Double-sided Silicone Coating | 0.8 | 0.0315 | 1050±30 | 32.05 |
| Other thicknesses can be customized according to your Requirements | ||||