0.3mm Thickness Insulation Binding Tape Polyester Resin Impregnated Fiberglass Web Banding Tape
1. Introduction:
Jiangnan is offered from stock in two standards, Type F and H.Types
F for use on Class F motors (155°C). Type F is for use when hot
armature banding and contains a nominal 27% and 32% resin and is
for use when banding cold armatures, though it can also be used on
hot armatures. Top performance can be obtained with class F, but
the application techniques appropriate to must be observed. It is
for use in applications up to 155°C where excessive moisture and
temperature are critical factors.
2. Specification
Type | (mm) Thickness | (mm) Tolerance | (mm) Width | (mm) Tolerance | Put up |
H200
| 0.20 | ±0.03 | 10 | ±1 | pancake or spool |
| 15 | ±1.5 | ||||
| 0.30 | ±0.03 | ||||
| 20.25.30.50.60 | ±2 |
3. Curing condition(Time to bring the piece to temperature is not
considered)
Temperature | ℃ | 160 | 150 | 135 | 120 | 115 |
Time | Hours | 2.5 | 3 | 5 | 14 | 20 |
4. Storage stability
| Temperature | oC | 10 | 15 | 20 | 30 |
| Time | Months | 20 | 15 | 10 | 6 |
5. Properties
Item | Unit | Figure | ||
Type | — | H200 | F150- | |
Thermal class | — | H(200℃) | F(155℃) | |
Volatile content | % | ≤2 | ||
Loss of weight at calcination | % | 26±2 | ||
Soluble resin content | % | ≥90 | ||
Tensile strength before curing | N/cm | 0.20mm | ≥1200 | ≥1000 |
| 0.30mm | ≥2000 | ≥1500 | ||
Maximum pull while banding | N/cm | 0.20mm | ≥600 | ≥500 |
| 0.30mm | ≥1000 | ≥800 | ||
Tensile strength of ringlike sample at room temperature after curing | Mpa | 20℃ | ||
| ≥1000 | ≥900 | |||
Tensile strength of ringlike sample at working temperature after curing | Mpa | 200℃ | 155℃ | |
| ≥700 | ≥560 | |||
Proof tracking index | V | ≥500 | ||
Arc resistance | S | ≥160 | ||
Dielectric strength | KV/mm | ≥12 | ||
Thermosetting | — | OK | ||
Loss of tensile strength after soaked in oil | % | ≤10 | ||
6. Features:
The banding tape is pliable and tacky. Its web structure provides easy unwind without glass trands separation and overlapping. The product contributes the characteristics of high tensile strength, high resistance to shocks, high modulus of elasticity, dimensional stability as well as no magnetically confining and eddy currents losses,
7. Application fields:
This kind of Fiberglass Banding tape can be widely used as ideal
banding materials for electrical motors, transformers and lightning
Rotor banding Large-transformer banding Transformer banding