0.3mm Epoxy Resin Impregnated Unidirectional Fiberglass Banding Tape Impregnated Fiberglass Banding Tape Class F
1. Introduction:
Jiangnan provides an electrical grade, parallel glass banding
tape, impregnated with an uncured, high temperature, modified
polyester resin. The glass fibers used in this tape are specially
treated to improve moisture resistance.
During cure, resin flow fills voids and air spaces, producing a homogeneous laminate with a smooth resin rich surface. The thermosetting modified polyester resin provides excellent arc resistance and minimizes flashover
2. Specification
| Size-Width | 3/4" |
| Product Type | Class F |
| Colour | White |
| Temperature Class | Class F-155 |
| Material | Polyester/Glass |
| Thickness | 11 mils |
3. Curing condition(Time to bring the piece to temperature is not
considered)
Temperature | ℃ | 160 | 150 | 135 | 120 | 115 |
Time | Hours | 2.5 | 3 | 5 | 14 | 20 |
4. Storage stability
| Temperature | oC | 10 | 15 | 20 | 30 |
| Time | Months | 20 | 15 | 10 | 6 |
5. Properties
Item | Unit | Figure | ||
Type | — | H200 | F150- | |
Thermal class | — | H(200℃) | F(155℃) | |
Volatile content | % | ≤2 | ||
Loss of weight at calcination | % | 26±2 | ||
Soluble resin content | % | ≥90 | ||
Tensile strength before curing | N/cm | 0.20mm | ≥1200 | ≥1000 |
| 0.30mm | ≥2000 | ≥1500 | ||
Maximum pull while banding | N/cm | 0.20mm | ≥600 | ≥500 |
| 0.30mm | ≥1000 | ≥800 | ||
Tensile strength of ringlike sample at room temperature after curing | Mpa | 20℃ | ||
| ≥1000 | ≥900 | |||
Tensile strength of ringlike sample at working temperature after curing | Mpa | 200℃ | 155℃ | |
| ≥700 | ≥560 | |||
Proof tracking index | V | ≥500 | ||
Arc resistance | S | ≥160 | ||
Dielectric strength | KV/mm | ≥12 | ||
Thermosetting | — | OK | ||
Loss of tensile strength after soaked in oil | % | ≤10 | ||
6. Features:
The banding tape has good moiisture resistance, smooth surface, excellent arc resistance and minimizes flashover.
7. Application fields:
This kind of Fiberglass Banding tape can be widely used as ideal
banding materials for electrical motors, transformers and large
equipment
Rotor banding Large-transformer banding Transformer banding