03mm Class H Polyester Resin Impregnated Glass Fiber Insulation Banding Tape For Motors And Generators
1. Introduction:
Jiangnan is offered from stock in two standards, Type F and
H. Type H is for use on motors of temperature ranges up to and
including Class H Plus (200° C). Armatures can be banded with this
tape either hot or cold. This resin flow also results in greater
prestress retention, thereby minimizing coil movement.
2. Specification
| Properties | Standard |
| Width | 25±2 |
| Thickness | 0.30±0.03 |
| Volatile content | ≤2 |
| Resin content | 26±2 |
| Soluble resin content | ≥90 |
| Tensile strength | ≥2000 |
| Refered to total cross section of Glass-resin tape measured at 20oC | ≥1000 |
| Refered to total cross section of Glass-resin tape measured atc150oC | ≥700 |
3. Curing condition(Time to bring the piece to temperature is not considered)
Temperature | ℃ | 160 | 150 | 135 | 120 | 115 |
Time | Hours | 2.5 | 3 | 5 | 14 | 20 |
4. Storage stability
Storage temperature | ℃ | 10 | 15 | 20 | 30 | |
Time | H200 | Months | 24 | 18 | 12 | 8 |
| F150 | 20 | 15 | 10 | 6 | ||
5. Properties
Item | Unit | Figure | ||
Type | — | H200 | F150- | |
Thermal class | — | H(200℃) | F(155℃) | |
Volatile content | % | ≤2 | ||
Loss of weight at calcination | % | 26±2 | ||
Soluble resin content | % | ≥90 | ||
Tensile strength before curing | N/cm | 0.20mm | ≥1200 | ≥1000 |
| 0.30mm | ≥2000 | ≥1500 | ||
Maximum pull while banding | N/cm | 0.20mm | ≥600 | ≥500 |
| 0.30mm | ≥1000 | ≥800 | ||
Tensile strength of ringlike sample at room temperature after curing | Mpa | 20℃ | ||
| ≥1000 | ≥900 | |||
Tensile strength of ringlike sample at working temperature after curing | Mpa | 200℃ | 155℃ | |
| ≥700 | ≥560 | |||
Proof tracking index | V | ≥500 | ||
Arc resistance | S | ≥160 | ||
Dielectric strength | KV/mm | ≥12 | ||
Thermosetting | — | OK | ||
Loss of tensile strength after soaked in oil | % | ≤10 | ||
6. Features:
Resiglass banding tape offers outstanding properties and performance, including high tensile strength, easy in application.
It is made up of high strength glass yarn impregnated with high temperature resistant thermoset polyester resin.
7. Application fields:
As class 200°c insulation its used for motor coils and transformer
cores and coils, to withstand the mechanical stress during
operation.