Indoor WPC Composite Wall Cladding , Composite Wood Wall Covering Yellow
Description:
Characteristic of Composite Wood Wall Covering :
| 1 | Environmental materials,recyclable |
| 2 | Saving time - easy maintenance and installation |
| 3 | Longer usage/life cycle - moistureproof |
| 4 | Stronger and more Flexible |
| 5 | Standard woodworking tools can be used |
| 6 | High degree of UV and color stability |
| 7 | Dimension stability against moisture and temperature.suitable from -40 to 60 |
| 8 | Weather resistant, suitable from -40 to 60 |
| 9 | Green ecological, Innovative technology, Lifestyle |
| 10 | Elegant nature wood grain texture and touch, with wood scent |
| 11 | Elegant and detailed shape design |
All the standard embossing is available with this option.
It offers the best combination of price and quality.
Different surface treatment options are available as added features.
The unique embossing patterns enhance the beauty of the boards,
as well as adding to its authenticity.
Beauty/Strong/Dependable.
Specifications:
Name | Composite Wood Wall Covering |
Size | 30cm x 30cm |
Length | 3m, 5m or Customized |
Color | Beige |
Material component | 60% PVC+30% Wood Powder+10% special additives |
Surface | Brushed, Scratched, Grain optional |
Warranty | 15years |
Certificate | ISO9001, ISO14001, CE, SGS |
Lifetime | 25years |
Package | pallet with PVC soft flim |
Range of use | Garden, Lawn, Balcony, Corridor, Garage, Pool&SPA Surrounds, Boardwalk, Playground |
Zhejiang Huaxiajie Macromolecule Building
Material Co., Ltd., which was established in 2004, is a special
manufacturer of PVC wall and Indoor Deck Materials , PVC doors and doorframes, and plastic-wood skirting and flooring.
Our products are environment friendly.
With advanced production lines from Germany and Italy, we have a
total annual capacity of over 5 million square meters PVC wall and
ceiling panels, over 6,000MT plastic-wood products, and over
2,000MT other PVC products.
Test Reprot:
Table 2.Test Results
Test Method | Characters | Result |
ASTM G155 | Weathering Resistance | After 2000hours weathering test Grey scale:3 There was some color changer on the surface. |
Table 2
Test Method | Characters | Result | ||
ASTM D 256 | Impact resistance | 59.1 J/m Break type Complete break | ||
ASTM D 790 | Flexural strength (Thickness:3mm,span:48mm) | MOR::79.8Mpa MOE:3107Mpa | ||
ASTM D1037 | Water absorption and Swelling in thickness (24hours immersion) | Water absorption:0.16% Swelling thickness:0.10% | ||
ASTM D2395 | Specific gravity | 1.17g/cm3 | ||
ASTM D4060 | Abrasion Resistance (CS-17,2000cycles) | Weight Loss:0.12g | ||
ASTM D696 | Coefficient of linear thermal expansion (-30℃~30℃) | 5.13*10-5 1/℃ | ||
ASTM D2394 | Slip Resistance Test |
| Static Slip Resistance | Dynamic Slip Resistance |
Dry surface | 0.63 | 0.45 | ||
Wet Surface | 0.69 | 0.68 | ||
ASTM D638 | Tensile strength | 37.2MPa | ||
ASTM D7032and ASTM D6109 | Flexural strength:Initial (Thickness:27mm,span 432mm) | MOR:33.2Mpa MOE:2073Mpa | ||
Flexural strength Temperature and moisture effects(-29℃ for 7days) | MOR:35.0Mpa,increase 5.4% MOE:2209Mpa, increase 6.6% | |||
Flexural strength Temperature and moisture effects(52℃ for 7days) | MOR:35.2Mpa,increase 6.0% MOE:2162Mpa, increase 4.3% | |||
Flexural strength Temperature and moisture effects(immersing in water for 7days) | MOR:33.4Mpa,increase 0.6% MOE:2103Mpa, increase 1.4% | |||
ASTM D7031 and ASTM D6109 | Flexural strength (Thickness:27mm,span:432mm) (After freeze-thaw resistance) | MOR:33.4Mpa,increase 6.0% MOE:2167Mpa, increase 4.5% | ||
ASTM D1761 | Fastener withdrawal test | 2387.8N | ||