Black Heat Shrink 6 Core Breakout Made Of Cross Linked Polyolefin
・ Made of cross linked polyolefin to provide mechanical protection and strain relief
・ Inner coated with adhesive on the body and the fingers to form a durable watertight seal
・ To provide sealing protection over 6-core cable crutch, such as trailing cable, variable frequency drive cable, telecommunication cables, control
cable, etc.
・ Shrink temperature: start at 90°C,and fully recovered at 130°C
Selection Table
| Product No. | ID as supplied/mm | ID after recovered/mm | ||||
| Body | Fingerdiameter | I Full length LU | Finger length (FL) (±5) | Body diameter | Finger diameter | |
| diameter (D) | Big finger(D2) Small finger(D1) | I | Big finger(D2) Small finger(D1) | |||
| WRSZT6-86/40(1#) | ■ 86 | N32 | "20 | 220 | 55 | W40 | W11 | W8 |
| WRSZT6-133/53(2#) | »33 | 355 | ^31 | 220 | 55 | W53 | W16 | W11 |
Technical Data
| Property | Test Method | Typical Value |
| Tensile Strength | ASTM-D-638 | Nl2MPa |
| Elongation at Break | ASTM-D-638 | 5:300% |
| Tensile Strength after Aging (12O'C,168hrs) | ASTM-D-638 | ^10MPa |
| Elongation at Break after Aging (120°C,168hrs) | ASTM-D-638 | M230% |
| Dielectric Strength | I EC 60243 | M15 kV/mm |
| Water Absorption | ISO 62 | W0.5% |
| Volume Resistivity | IEC 60093 | x 1013Q ・ cm |