5.5mm Green Thin Wall Halogen Free Flexible Heat Shrink Tubing
Ultra thin wall halogen free.flexible very well.
2:1 Heat shrink tubing with low moq and short lead time .
Very high quality heat shrink tubing from manufacture .
Features
• Thin wall Wall With out Adhesive and very Soft.
• Halogen free
• Flame retardant
• low smoke generation if burning
• Continuous operating
• Temperature:-55°C to 125°C
• Fully shrink temperature: 110°C
• RoHS and Sony compliant
Dimensions
| Size | As Supplied | After Recovery | Standard Package | ||
| Inch | mm | Internal Diameter mm | Internal Diameter mm | Wall Thickness mm | Spool Length M/spooF |
| 1/16 | 1.0 | 1.4±0.2 | 0.65 | 0.20 | 200 |
| 1.5 | 1.9+0.2 | 0.85 | 0.20 | 200 | |
| 3/32 | 2.0 | 2.4±0.2 | 1.00 | 0.22 | 200 |
| 2.5 | 2.9±0.2 | 1.30 | 0.25 | 200 | |
| 1/8 | 3.0 | 3.4±0.2 | 1.50 | 0.28 | 200 |
| 3.5 | 3.9±0.2 | 1.80 | 0.28 | 200 | |
| 4.0 | 4.410.2 | 2.00 | 0.30 | 200 | |
| 3/16 | 4.5 | 4.9±0.2 | 2.30 | 0.30 | 100 |
| 5.0 | 5.5±0.2 | 2.5 | 0.32 | 100 | |
| 1/4 | 6.0 | 6.5±0.2 | 3.0 | 0.32 | 100 |
| 5/16 | 7.0 | 7.5±0.3 | 3.5 | 0.32 | 100 |
| 8.0 | 8.5±0.3 | 4.0 | 0.32 | 100 | |
| 3/8 | 9.0 | 9.5+0.3 | 4.5 | 0.35 | 100 |
| 10.0 | 10.5±0.3 | 5.0 | 0.35 | 100 | |
| 11.0 | 11.5±0.3 | 5.5 | 0.40 | 100 | |
| 1/2 | 12.0 | 12.5±0.3 | 6.0 | 0.40 | 100 |
| 13.0 | 13.5±0.3 | 6.5 | 0.40 | 100 | |
| 14.0 | 14.5±0.3 | 7.0 | 0.40 | 100 | |
| 5/8 | 15.0 | 15.5±0.4 | 7.5 | 0.40 | 100 |
| 16.0 | 16.5±0.4 | 8.0 | 0.40 | 100 | |
| 17.0 | 17.5±0.4 | 8.5 | 0.40 | 100 | |
| 3/4 | 18.0 | 18.5±0.4 | 9.0 | 0.42 | 100 |
| 20.0 | 20.5±0.5 | 10.0 | 0.45 | 100 | |
| 22.0 | 22.5±0.5 | 11.0 | 0.45 | 100 | |
| 1 | 25.0 | 25.5±0.5 | 12.5 | 0.45 | 50 |
Technical Data
| I Property I | Test Method | Typical Performance I |
| Tensile strength(MPa) | ASTM D 2671 | >10.4 |
| Ultimate elongation(%) | ASTM D 2671 | >200 |
| Tensile strength after heat aged (Mpa) | 158°CX168h | N7.3 |
| Ultimate elongation after heat aged (%) | 158°CX168h | ^100 |
| Longitudinal change(%) | ASTM D 2671 | -5%~+5% |
| Flammability | ASTM D 2671 C method | VW-1 |
| Dielectric strength (kV/mm) | ASTM D 149 | >15 |
| Volume resistivity (Q-cm) | ASTM D 876 | ^1014 |