EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip
In Coil
DIN 1.4568 is a corrosion resistant stainless steel with
good formability in soft condition.
The work hardening is greater than other austenitic stainless
steels, similar to 1.4310.
The use of 1.4568 stainless is indicated, if stress applied
parts were exposed to higher temperatures
or if spring parts have to be formed in soft condition with
additional hardening.
DIN 1.4568 stainless strip in annealed condition shows low
magnetism witch increases with cold forming.
Typical applications
In hard condition: Highly stressed spring parts. Spring parts
exposed to higher temperature.
In soft condition: Spring parts which have to be formed in soft
condition (spring back effect).
Precipitation hardening steel, Stainless Chromium – Nickel - Steel |
Chemical composition ( typical weight % )
Grade | C | Si | Mn | Cr | Ni | Al |
1.4568 | 0.07 | 0.60 | 0.80 | 17.0 | 7.0 | 1.0 |
Product forms
1.4568 stainless is produced as narrow strip ( precision strip ) in
the thickness range from 0.1 mm to 3.0 mm.
The possible width is in between 5 mm to 420 mm, Tolerances are in
accordance to DIN EN ISO 9445.
Possible conditions for delivery are:
Solution annealed (soft) in accordance to DIN EN 10 088 – part 2,
procedure 2R, or work hardened (hard) in
accordance to DIN EN 10151 procedure 2H with tensile strength up to
maximum 1800 MPa.
Grade | Solution Annealed | +C1000 1/2H | +C1150 3/4H | +C1300 4/4H | +C1500 5/4H | +C1700 K1 |
1.4568 | Tensile strength 800~1000 Mpa | 1000~1150 Mpa | 1150~1300 Mpa | 1300~1500 Mpa | 1500~1700 Mpa | 1700~1900 Mpa |
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com