PVC Waterproof Membrane is one kind of polymer waterproof with high
quality, it is made from polyvinyl chloride resin, mixed with
plasticizer, filler, antioxygen, ultraviolet absorber and other
auxiliaries.
Specification |
No. | Items | Technical Data |
H | L | P | G | GL |
1 | Upper Resin Thickness | | ≥0.40mm |
2 | Tensile Property | Max. Tension (N/cm) | - | ≥120 | ≥250 | - | ≥120 |
Tensile Strength (MPa) | ≥10 | - | - | ≥10 | - |
Elongation /Max. Tension | - | - | ≥15% | - | - |
Breaking Elongation | ≥200% | ≥150% | - | ≥200% | ≥100% |
3 | Dimensional Changing when Heating | ≤2.0% | ≤1.0% | ≤0.5% | ≤0.1% | ≤0.1% |
4 | Low Temperature Flexibility | -25℃, No cracking |
5 | Impermeability | 0.3Mpa, 120 Minutes, No leaking |
6 | Shock Resistance | 0.5kg·m, No leaking |
7 | Static Load Resistance | - | - | 20kg, No leaking |
8 | Joint Peel Strength (N/mm) | ≥4.0 | ≥3.0 |
9 | Right-angled Tearing Strength (N/mm) | ≥50 | - | - | ≥50 | - |
10 | Trapezoid Tearing Strength (N) | - | ≥150 | ≥250 | - | ≥220 |
11 | Water Absorption Coefficient | After dipping | 70℃, 168 hours, ≤4.0% |
After sun-cure | 70℃, 168 hours, ≥-0.40% |
12 | Thermal Aging (80℃) | Time | 672 hours |
Appearance | No bubbling, cracking, layering, cohering or holes |
Holding / Max. Tension | - | ≥85% | ≥85% | - | ≥85% |
Tensile Strength Holding | ≥85% | - | - | ≥85% | - |
Elongation Holding / Max. Tension | - | - | ≥80% | - | - |
Breaking Elongation Holding | ≥80% | ≥80% | - | ≥80% | ≥80% |
Low Temperature Flexibility | -20℃, No cracking |
13 | Chemical Resistance | Appearance | No bubbling, cracking, layering, cohering or holes |
Holding / Max. Tension | - | ≥85% | ≥85% | - | ≥85% |
Tensile Strength Holding | ≥85% | - | - | ≥85% | - |
Elongation Holding / Max. Tension | - | - | ≥80% | - | - |
Breaking Elongation Holding | ≥80% | ≥80% | - | ≥80% | ≥80% |
Low Temperature Flexibility | -20℃, No cracking |
14 | Artificial Weathering Aging | Time | 1500 hours (single-ply roofing 2500 hours) |
Appearance | No bubbling, cracking, layering, cohering or holes |
Holding / Max. Tension | - | ≥85% | ≥85% | - | ≥85% |
Tensile Strength Holding | ≥85% | - | - | ≥85% | - |
Elongation Holding / Max. Tension | - | - | ≥80% | - | - |
Breaking Elongation Holding | ≥80% | ≥80% | - | ≥80% | ≥80% |
Low Temperature Flexibility | -20℃, No cracking |
Product Features:
1) Long life, aging-resistant, roofing materials can be over 20
years, and if underground use it can be 50 years.
2) High tensile strength, high extensibility, small dimensional
change when heat treatment.
3) Good flexibility under low temperature, good variability to be
adaptable to temperature difference of the environment.
4) Good rootage penetration resistibility, suitable to be used for
planted roof.
5) Good perforating resistibility.
6) Convenient for construction, weldable, firm and secure,
environmental protective and pollution free.
7) Strong chemical resistance, adaptable to special situations.
8) Good plasticity, convenient and fast treatment on delicate parts
of corners and edges.
9) Easy maintenance, low cost.
Application:
1) Roof construction and steel structure of both industrial and
civil engineering.
2) Underground engineering, such as subways, tunnels, air Raid
shelter, etc.
3) Other projects, for example, dam, water reservoir, artificial
lake, roof for plant and others.
Storage and Transportation:
1) Separate storage for different models.
2) Temperature should be below 45℃.
3) Avoid direct sunshine, rain, keep ventilated.
Thickness: 1.2mm, 1.5mm, 2.0mm
Width: 2.05m, or customized width
Length: 20m, or customized width
Color: White, Green, Blue, or customized color