High 170 TG double sided pcb , FR4 Mixed Rogers Satellite Radio PCB 0.8 mm
Products Details
| Raw Material | FR-4 (Tg 170 available) |
| Layer Count | 2-Layer |
| Board Thickness | 0.8mm |
| Copper Thickness | 1.0oz |
| Surface Finish | ENIG(Electroless Nickel Immersion Gold) |
| Solder Mask | Black |
| Silkscreen | White |
| Min. Trace Width/Spacing | 0.075/0.075mm |
| Min. Hole Size | 0.25mm |
| Hole Wall Copper Thickness | ≥20μm |
| Measurement | 200×500mm |
| Packaging | Inner: Vacuum-packed in soft plastic bales Outer: Cardboard Cartons with double straps |
| Application | Communication,automobile,cell,computer,medical |
| Advantage | Competitive Price,Fast Delivery,OEM&ODM,Free Samples, |
| Special Requirements | Buried And Blind Via, Impedance Control, Via Plug, BGA Soldering And Gold Finger Are Acceptable |
| Certification | UL,ISO9001:2008,ROHS,REACH,SGS,HALOGEN-FREE |
Parameter:
| Model | Parameter | thickness(mm) | Permittivity(ER) |
| F4B | F4B | 0.38 | 2.2 |
| F4B | 0.55 | 2.23 | |
| F4B | 0.225,0.3,0.5,08,1,1.2,1.5,2,2.5,3.0 | 2.65 | |
| F4Bk | 0.8,1.5 | 2.65 | |
| F4B | 0.8 | 3.5 | |
| FE=F4BM | 1 | 2.2 | |
| Rogers | RO5880 | 0.254 0.508 0.762 | 2.20 ± 0.02 |
| RO4350 | 0.254 0.508,0.8,1.524 | 3.5 | |
| RO4003 | 0.508 | 3.38 | |
| TACONIC | TLF-35 | 0.8 | 3.5 |
| TLA-6 | 0.254,0.8,1,1.5, | 2.65 | |
| TLX-8 | 0.254,0.8,1,1.6 | 2.55 | |
| RF-60A | 0.64 | 6.15 | |
| TLY-5 | 0.254,0.508,0.8 | 2.2 | |
| TLC-32 | 0.8,1.5,3 | 3.2 | |
| TLA-35 | 0.8 | 3.2 | |
| ARLON | AD255C06099C | 1.5 | 2.55 |
| MCG0300CG | 0.8 | 3.7 | |
| AD0300C | 0.8 | 3 | |
| AD255C03099C | 0.8 | 2.55 | |
| AD255C04099C | 1 | 2.55 | |
| DLC220 | 1 | 2.2 |
PrePreg Material
| Parameter | Value |
| Specific gravity/density | 1.850 g/cm3 (3,118 lb/cu yd) |
| Water absorption | −0.125 in < 0.10% |
| Temperature index | 140 °C (284 °F) |
| Thermal conductivity, through-plane | 0.29 W/(m·K), 0.343 W/(m·K) |
| Thermal conductivity, in-plane | 0.81 W/(m·K), 1.059 W/(m·K) |
| Rockwell hardness | 110 M scale |
| Bond strength | > 1,000 kg (2,200 lb) |
| Flexural strength (A; 0.125 in) - LW | > 440 MPa (64,000 psi) |
| Flexural strength (A; 0.125 in) - CW | > 345 MPa (50,000 psi) |
| Tensile strength (0.125 in) LW | > 310 MPa (45,000 psi) |
| Izod impact strength - LW | > 54 J/m (10 ft·lb/in) |
| Izod impact strength - CW | > 44 J/m (8 ft·lb/in) |
| Compressive strength - flatwise | > 415 MPa (60,200 psi) |
| Dielectric breakdown (A) | > 50 kV |
| Dielectric breakdown (D48/50) | > 50 kV |
| Dielectric strength | 20 MV/m |
| Relative permittivity (A) | 4.8 |
| Relative permittivity (D24/23) | 4.8 |
| Dissipation factor (A) | 0.017 |
| Dissipation factor (D24/23) | 0.018 |
| Dielectric constant permittivity | 4.70 max., 4.35 @ 500 MHz, 4.34 @ 1 GHz |
| Glass transition temperature | Can vary, but is over 120 °C |
| Young's modulus - LW | 3.5×106 psi (24 GPa) |
| Young's modulus - CW | 3.0×106 psi (21 GPa) |
| Coefficient of thermal expansion - x-axis | 1.4×10−5 K−1 |
| Coefficient of thermal expansion - y-axis | 1.2×10−5 K−1 |
| Coefficient of thermal expansion - z-axis | 7.0×10−5 K−1 |
| Poisson's ratio - LW | 0.136 |
| Poisson's ratio - CW | 0.118 |
| LW sound speed | 3602 m/s |
| SW sound speed | 3369 m/s |
| LW Acoustic impedance | 6.64 MRayl |
Competitive Advantage:
1) With UL,ROHS,ISO,IPC
2).Lead time:3-10 working days
3)Competitive price best quality
4).Rich 20 years experience in High Tg Multilayer PCB .
What Information customer need to provide for quotation ?
1. PCB Gerber files ,protel,powerpcb,Autocad,etc.
2. BOM list for PCB assembly.
3. Send us your sample PCB or PCBA.
4. OEM is acceptable.