Good Deep drawing property 3104 H19 aluminum plate for beverage cans
Description:
| Alloy | 3104 |
| Temper | H 19 |
| Thickness | 0.28-0.35 mm |
| Width | 200-2600 mm |
| Standard | YS/T 435--2000 |
3104-H19 aluminum is a type of 3104 aluminum. It is furnished in the H19 temper. To achieve this temper, the metal is strain hardened to a strength that exceeds H18 by at least 10 MPa (or 1.5 ksi). The graph bars on the material properties cards below compare 3104-H19 aluminum to: 3000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). The length of each bar shows the given value as a % of the largest value in the relevant set.
| Physical Properties | Metric | English |
| Density | 2.72 g/cc | 0.0983 lb/in³ |
| Mechanical Properties | Metric | English |
| Hardness, Brinell | 78 | 78 |
| Hardness, Knoop | 101 | 101 |
| Hardness, Vickers | 88 | 88 |
| Tensile Strength, Ultimate | 290 MPa | 42100 psi |
| Tensile Strength, Yield | 260 MPa | 37700 psi |
| Elongation at Break | 4.00% | 4.00% |
| Modulus of Elasticity | 69.0 GPa | 10000 ksi |
| Poissons Ratio | 0.34 | 0.34 |
| Shear Modulus | 26.0 GPa | 3770 ksi |
| Shear Strength | 175 MPa | 25400 psi |
| Electrical Properties | Metric | English |
| Electrical Resistivity | 0.00000400 ohm-cm | 0.00000400 ohm-cm |
| Thermal Properties | Metric | English |
| CTE, linear | 23.8 µm/m-°C | 13.2 µin/in-°F |
| 25.4 µm/m-°C | 14.1 µin/in-°F | |
| Specific Heat Capacity | 0.880 J/g-°C | 0.210 BTU/lb-°F |
| Thermal Conductivity | 170 W/m-K | 1180 BTU-in/hr-ft²-°F |
| Melting Point | 630 - 655 °C | 1170 - 1210 °F |
| Solidus | 630 °C | 1170 °F |
| Liquidus | 655 °C | 1210 °F |
| Component Elements Properties | Metric | English |
| Aluminum, Al | 95 - 98.4 % | 95 - 98.4 % |
| Copper, Cu | 0.05 - 0.25 % | 0.05 - 0.25 % |
| Gallium, Ga | <= 0.05 % | <= 0.05 % |
| Iron, Fe | <= 0.80 % | <= 0.80 % |
| Magnesium, Mg | 0.80 - 1.3 % | 0.80 - 1.3 % |
| Manganese, Mn | 0.80 - 1.4 % | 0.80 - 1.4 % |
| Other, each | <= 0.05 % | <= 0.05 % |
| Other, total | <= 0.15 % | <= 0.15 % |
| Silicon, Si | <= 0.60 % | <= 0.60 % |
| Titanium, Ti | <= 0.10 % | <= 0.10 % |
| Vanadium, V | <= 0.05 % | <= 0.05 % |
| Zinc, Zn | <= 0.25 % | <= 0.25 % |