5182 aluminum is a 5000-series aluminum alloy, the main alloying addition is magnesium. And it's a wrought alloy type with good corrosion resistance.
| Element | Content (%) |
|---|---|
| Aluminum, Al | 95.2 |
| Magnesium, Mg | 4.5 |
| Manganese, Mn | 0.35 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 275 MPa | 39900 psi |
| Yield strength | 130 MPa | 18900 psi |
| Elongation at break (thickness 1.60 mm/0.0630 in) | 21% | 21% |
| Elastic modulus | 69.6 GPa | 10100 ksi |
| Shear modulus | 26 GPa | 3770 ksi |
| Poisson’s ratio | 0.33 | 0.33 |
| Hardness, Brinell | 74 | 74 |
| Hardness, Knoop (converted from Brinell hardness value) | 97 | 97 |
| Hardness, Vickers (converted from Brinell hardness value) | 84 | 84 |
| Latent Heat of Fusion | 390 J/g |
| Maximum Temperature: Mechanical | 180 °C |
| Melting Completion (Liquidus) | 640 °C |
| Melting Onset (Solidus) | 590 °C |
| Specific Heat Capacity | 900 J/kg-K |
| Thermal Conductivity | 130 W/m-K |
| Thermal Expansion | 24 µm/m-K |