Home Companies DONGGUAN YUYANG INSTRUMENT CO., LTD

Plastic Material ASTM D1238 Flammability Testing Equipment / Melt Flow Index Tester Color With Touch Screen Display

Contact Us

[China]

Trade Verify

Address: B1505, FORTUNE PLAZA, No.1, Yuanmei Road, Nancheng District, Dongguan City, Guangdong Province, China

Contact name:Seline Yu

DONGGUAN YUYANG INSTRUMENT CO., LTD

Verified Suppliers

Trust
Seal
Verified
Supplier
Credit
Check
Capability
Assessment

Plastic Material ASTM D1238 Flammability Testing Equipment / Melt Flow Index Tester Color With Touch Screen Display

Country/Region	china
City & Province	dongguan guangdong
Categories	Solar Chargers

Product Details

Plastic Material ASTM D1238 Melt Flow Index Tester Color Touch Screen Display

Application:

XNR-400C plastic material melt flow index mfi testing machine/ Mfi tester is accordance to ISO1133;GB3682 2000,ASTM D1238.
It's suitable to measure melt flow character of PP, PE, POM, ABS plastics and plastic
productions, widely used in factories, products quality testing station, scientific and research
institutes, and concerned industries.

Specification:

Type	YY166
Squeeze out the part of material
Discharge port diameter	Φ2.095±0.005mm
The length of the discharge port	8.000±0.025mm
Loaded barrel diameter	Φ9.550±0.025mm
Loaded barrel length	152±0.1mm
The diameter of the piston rod head	9.475±0.015mm
The length of the piston rod head	6.350±0.100mm
1, Standard Test load (eight)
Ⅰ	0.325kg = (piston rod + weight tray + insulation sleeve + weight body)
Ⅱ	1.200 kg = (0.325 +2 No. 0.875 weight)
Ⅲ	2.160 kg = (0.325 + 1.835 weight)
Ⅳ	3.800 kg = (0.325 +4 3.475 weight)
Ⅴ	5.000 kg = (0.325 +5 No. 4.675 weights)
Ⅵ	10.000 kg = (0.325 +5 No. 4.675 weight + 5.000 weight)
Ⅶ	12.500 kg = (5.000 +7 2.500 0.325 +5 4.675 weight +6 weights)
Ⅷ	21.600 kg, = (0.325 +2 No. 0.875 + 1.835 )
Measurement	MFR and MVR and Density
Thermostat range	Room temperature - 400 ° C
Temperature accuracy	±0.2°C
Temperature resolution	0.1°C
Timing range	0.1-999 s
Timing accuracy	0.1s
Cut material way	Automatic or manual cut material way
Display	Color touch screen
Print	Can print the test report
Working conditions	Ambient temperature of 10 ° C -40 ° C; Relative humidity of 30% -80%
Instrument Dimensions	4500×400×610(L × W × H)

The test method includes determining the rate of extrusion of molten thermoplastic resins with the help of an extrusion plastomer. Once preheated at a specified, resin is extruded through a die with a specified length and orifice diameter under prescribed conditions of temperature, load, and piston position of the barrel. There are several procedures used in ASTM D1238 standard test method:

Procedure A determines the melt flow rate (MFR) of a thermoplastic material, measure in grams of material/10 minutes (g/10 min). The method is based on the measurement of the mass of material extruding from the die over a given period of time. The procedure is applicable for materials with melt flow rates between 0.15 and 50 g/10 min.
Procedure B determines the MFT and melt flow volume rate of thermoplastic materials and is used for materials that have flow rate from 0.50 to 1500 g/10 min.
Procedure C determines the MFT of polyolefin materials and is also used an alternative to procedure B that has melt flow rate more than 75 g/10 min. This method uses modified die (referred to as a half-die).
Procedure D is referred as “Flow Rate Ratio” (FRR) test that determines MFR using two or three different test loads (either increasing or decreasing the load during the test) on one charge of material.

Melt Flow Index Tester Complied with ASTM D1238 Standard Test Method

Presto’s Melt Flow Index Tester evaluated the flow properties of the molten plastics or resins and defined as the rate of flow (in grams per 10 minutes) of extrudates of molten resins through a jet of a specific length and diameter. The test is performed under suggested conditions of load, temperature and piston position in a cylindrical cavity inside a heated metallic tube barrel.