Fused alumina, magnesium aluminate spinel, fused MgO and graphite are the main raw materials in use for Low carbon corundum-spinel brick. Low carbon corundum-spinel bricks, featured with high strength, better corrosion resistance and thermal shock resistance, are mainly used in the bottom and sidewall for low and ultra-low carbon steel production.
This series of high temperature kiln refractory High Temp Fire
Brick use special grade aluminum bauxite clinker as the main raw
material, supplemented by special additives, high pressure forming
and high temperature firing. Refractory bricks alumina has the
characteristics of large heat storage capacity and small creep
rate.
The High Temp Fire Brick made by CH refractories with very widely
application and various size with free mold charge to meet
different kiln applications. To be professional High Temp Fire
Brick manufacturer since 1984, CH refractories provides alumina
lining bricks not only can design fire furnace bricks size
according to your kiln or furnace drawing for free, but also
suggest you the most economical refractory furnace alumina bricks
price for your kiln or furnace. Generally , there are three levels
lime kiln refractory high alumina brick in our plant, just please
inform bricks working condition, CH refractories will suggest you
the most suitable alumina refractory bricks to save your money and
achieve the best performance.
Product code | CH-LMT80 | CH-LMT85 | CH-LMT88 |
Al2O3/% | 80 | 85 | 88 |
MgO/% | 5 | 4 | 3 |
C/% | 5 | 5 | 5 |
Apparent porosity/% | 8 | 8 | 8 |
Bulk density/g.cm3 | 2.90 | 2.95 | 3.0 |
Cold Crushing Strength/MPa | 35 | 40 | 45 |
Application | The sidewall and bottom of ladle working lining for low carbon steel production |