Copper beryllium strips C17200 for relays stamping parts and switches
Product brief introduction:
Beryllium cooper strip is widely used in producing all kinds of
micromotor’s brush, switch, relay, cell phone battery,
spring,connector, attemperator’s leaf spring which with high
strength, high elasticity, high hardness and high wearing feature.
Chemical Composition:
Be: 1.85-2.10%
Co+Ni: 0.20% Min.
Co+Ni+Fe: 0.60% Max.
Cu: Balance
Note: Copper plus additions equal 99.5% minimum.
Features:
1. Strength: by age-hardening, can reach up to 1500N/mm2 tensile strength, so it be used as elastic material which can tolerate high bending stress.
2. Electrical conductivity: According to different alloys, specification, about 20-70% IASC (international annealed copper standard) can be used as high density voltaic elastic material.
3. Machinability: Before age hardening, the material can be complicated formed processing.
4. Fatigue Strength: Have excellent anti-fatigue properties(Can be operate repeatedly), so be widely used in long-life and high-reliability accessories.
5. Heat resisting property: Can keep small Stress relaxation rate in the high temperature condition, so can be used under a large temperature range.
6. Corrosion resistance: In range of all copper alloy, it has
better corrosion resistance than Copper-Nickel Alloy,scarcely
initiate corrosion by environmental implication.
Beryllium copper strip Mechanical Properties:
| Symbol or Brands | Chemical Composition | Temper | Tensile Strength (N/mm2) | Elongation (%) | Endurance | Vickers Hardness (HV) | Electric Conductivity (%IACS) |
| C1720 | Be:1.8-2.0 Ni+Co≥0.20 Ni+Co+Fe≤0.6 Cu+Be+Co+Fe ≥99.5 | Before age-hardening | |||||
| O | 410-540 | ≥35 | - | 90-160 | ≥17 | ||
| 1/4H | 510-620 | ≥10 | - | 45-220 | ≥16 | ||
| 1/2H | 590-695 | ≥5 | - | 180-240 | ≥15 | ||
| H | 685-835 | ≥2 | - | 210-270 | ≥15 | ||
| After age-hardening | |||||||
| OT | 1100-1380 | ≥3 | ≥960 | 325-400 | ≥22 | ||
| 1/4HT | 1180-1400 | ≥2 | ≥1030 | 350-430 | |||
| 1/2HT | 1240-1440 | ≥2 | ≥1100 | 360-440 | |||
| HT | 1270-1480 | ≥1 | ≥1140 | 380-450 | |||
| Spread (Standard) | |||||||
| OM | 685-885 | ≥18 | ≥480 | 220-270 | ≥17 | ||
| 1/4HM | 735-930 | ≥10 | ≥550 | 235-285 | |||
| 1/2HM | 815-1010 | ≥8 | ≥650 | 260-310 | |||
| HM | 910-1110 | ≥6 | ≥750 | 295-345 | |||
| XHM | 1100-1290 | ≥2 | ≥930 | 340-390 | |||
| XMHS | 1210-1400 | ≥2 | ≥1030 | 360-410 | |||
Usage:
Casting beryllium bronze: (Cu-2Be-0.5Co-0.3Si,
Cu-2.6Be-0.5Co-0.3Si, Cu-0.5Be-2.5Co, etc.) For explosion-proof
tools, various molds (inner inserts for plastic injection molding
dies, integral cavities for blow molds, automotive molds),
bearings, bushings, bushings, gears and various electrodes
Processing beryllium bronze: (Cu-2Be-0.3Ni, Cu-1.9Be-0.3Ni-0.2Ti)
is mainly used as a variety of advanced elastic components,
especially requiring good conductivity, corrosion resistance, wear
resistance, cold resistance, various no magnetic components, used
as a large number of bellows, diaphragms, bellows, micro switches,
etc.
Technical Specification
Density | Hardness after Quenching | Tensile Strength | Yield Strength (0.2%) | Elastic Modulus |
Conductivity | Thermal Conductivity at 20℃ |
| g/cm | HRC | MPa | MPa | GPa | IACS | w/m.k |
| 8.3 | ≥36-42 | ≥1000 | 1035 | 128 | 18% | 105 |