Supermalloy magnetic shielding made by permalloy 80 strip Soft
Magnetic alloy
Product brief introduction
Ohmalloy-1J79 is a nickel–iron magnetic alloy, with about 80%
nickel and 20% iron content. Invented in 1914 by physicist Gustav
Elmen at Bell Telephone Laboratories, it is notable for its very
high magnetic permeability, which makes it useful as a magnetic
core material in electrical and electronic equipment, and also in
magnetic shielding to block magnetic fields. Commercial permalloy
alloys typically have relative permeability of around 100,000,
compared to several thousand for ordinary steel.
Normal composition%
| Ni | 78.5~80.0 | Fe | Bal. | Mn | 0.6~1.1 | Si | 0.3~0.5 |
| Mo | 3.8~4.1 | Cu | ≤0.2 | ||||
| C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
Typical Mechanical properties
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 980 | 1030 | 3~50 |
| The magnetic properties of alloys with high permeability in weak fields | ||||
| 1J79 | Initial permeability | Maximum permeability | Coercivity | Saturation magnetic induction intensity |
Cold-rolled strip/ sheet. Thickness, mm | μ0.08/ (mH/m) | μm/ (mH/m) | Hc/ (A/m) | BS/ T |
| ≥ | ≤ | |||
| 0.01 mm | 17.5 | 87.5 | 5.6 | 0.75 |
| 0.1~0.19 mm | 25.0 | 162.5 | 2.4 | |
| 0.2~0.34 mm | 28.0 | 225.0 | 1.6 | |
| 0.35~1.0 mm | 30.0 | 250.0 | 1.6 | |
| 1.1~2.5 mm | 27.5 | 225.0 | 1.6 | |
| 2.6~3.0 mm | 26.3 | 187.5 | 2.0 | |
| cold drawn wire | ||||
| 0.1 mm | 6.3 | 50 | 6.4 | |
| Bar | ||||
| 8-100 mm | 25 | 100 | 3.2 | |
Typical Physical properties
| Density (g/cm3) | 8.6 |
| Electrical resistivity at 20℃(Ωmm2/m) | 0.55 |
| Coefficient of linear expansion(20℃~200℃)X10-6/℃ | 10.3~11.5 |
| Saturation magnetostriction coefficient λθ/ 10-6 | 2.0 |
| Curie point Tc/ ℃ | 450 |