Master Models Tooling Paste Epoxy Resin Materials Packing 10kg 15kg
20kgs
Product main properties
This product is a two-component materials, by automatically output
device fast coating model, single coating thickness can be up to 40
mm, reaction put the quantity of heat low, coating and processing
when no smell, room temperature curing can be carried out after a
day of machining, machining performance is good, good surface
effect, material size stability is good
Product application
1. Wind-power blades can be applied to the model of the male die,
the cabin cover mould, automobile master model of casting mould
board, checking fixture production, foundry industry, sand core
boxes, and various modeling tools etc.
2. used for sheet metal forming mould, tensile modulus, rolling
zhong mold, mold, and the bending modulus.
3. used for foaming mould, vacuum forming mould, injection mould,
composite materials forming mould, etc
4. quick samples/hand: for small batch production of plastic
material.
Product operation process
Given according to the proportion of fully mixing thoroughly, the
same color. Try to avoid to produce bubbles, it is best to use
vacuum mixer mixing. Strict control, with a thick layer of a
coating is not more than 40 mm;If upset, after waiting for curing
the second floor. The after curing processing, performance is
better. (after curing: 80 ℃ + 8 h or 3 days) at room temperature,
curing can be after rough machining, precision work after 3
days;The material of metal, composite structure materials such as
sticky relay is extremely strong, mold release agents shall be used
for rolling over. Make sure the strength of the support frame,
stability and cleanness, machine
Introduction
Material | 5200A | 5200B | Mixed |
Description | epoxy resin | curing agent | |
mixing ration | 1 | 1 | |
Color: | Brown | Yellow | Brown |
mixed time:500g,25°(min) | 30 | ||
curing time before machining(20-25mm) (hours) | 6-8 | ||
layer thickness (mm) | max.40 | ||
Density:(g/cm³): | 0.7-0.8 | ||
Hardness(Shore D): | 65-70 | ||
Temperature Resistance(°C): | 70-75 | ||
Coefficient of Thermal Expansion(10-6 K-1): | 45-50 | ||
Compressive Strength(N/mm²): | 52 | ||
Flexural Strength(N/mm²): | 32 | ||
Tensile Strength(N/mm²): | 26 | ||
Package(kg) | 10 | 10 |
Characteristics:
easily shaped and machined,fine surface structure
Applications:
yacht model,benchmark model, system and sand-cast model, rapid
prototype,etc.