good tensile strength EVA film for architecture

Active Member

Contact Us

[China]

Address: XingLiXiong Building,Zhuji Rd,Dali Town,Nanhai Dist.,Foshan,528231,China

Contact name:Wendy

China E&N Film Technology Co.,Ltd

good tensile strength EVA film for architecture

Country/Region china
City & Province foshan guangdong
Categories Sport Product Agents

Product Details

Advanges:

 

1.Superior stability after breakage and High fracture integrity.

2.Cross-linking :85-95% (130-150°C)with good heat&humidty resistance.

3. Less overflowing: Milt index 5-6;

4. Superior water-proof: Open edge application

5. Better Sound insulation

6. Perfect sunlight control and UV filtering.

7. Crystalline particle control make EVA film more transparency and cleanliness.

 

 

Product Details:

 

1. The best mechanical performancet:
Cross-linkingExtracted in Xylene solution>95%(after150°C25mins laminating)
Tensile strength >21MPA
Adhesion with glass >95N/cm
Water absorption <0.1%
 
2. Superior optical performance:
Light transmittance>91%
Haze<0.2%
UV filtering99%
Light transmittance decrease<0.5%( 2000hrs UV radiation)
Yellow index (YI)<3 (2000hrs UV radiation)
 
3. Best durability an stability in outdoor climate application: Heat and humidity resistance, Radiation resistance, ball impact peeling test and shot bag impact have been tested for laminated glass with norminal thickness according to GB15763.3-2009 safety glazing materials in building-Part3: Laminated glass.
Boilding test (2rhrs into 100°C water)5mm glass+0.80mm EVA+5mm glassGood
Heat and Humidty resistance test85°C 85%RH,1000hrsGood
Anti-aging test50°C 65%RH,UV radiation 2000hrsGood
Heat and cold shock test-40°C30mins/80°C30mins, 50circlesGood
Impact resistance against shot-bagGB-15763.3-2009Qualified
Ball impact peeling resistanceGB*15763.3-2009Qualified
 

 

Laminating instructions:

1. Prepare and cut the EVA film into right size according to the following structure:

glass+EVA film + glass

2. Put the overlapped glass into silicon bag and seal silicon bag well.

3. Activate vacuum pump for 5-8min till vacuum value reach -0.095Mpa to double checking the vacuum is good.

4 Set up the laminating temp. and time and start heating.The following data based on 5mm glass +0.40mm EVA +5mm glass.

 Heating speedTemp. And holding timeVacuum value
First section2°C/ min6025mins-0.095MPA
Second section2°C/ min80°C30mins-0.095MPA
Third section2°C/ min135°C45mins-0.04MPA

Remark: The above curves only for reference, the user should do some adjusts according to the process surroudings(temperature and humidity), glass area, glass thicknes,glass type and the machine itself.

 

 

Packaging details:

vacuum plybag+tinfoil paper+carton box+3/4rolls into one plywood box

 

 

 

Certificate: SGS and ISO9001 and EN ISO 12543-4:1998 made by our agent

 

 

E&N company instruction:

 

Foshan E&N company as a high-tech and professional EVA film manufacturer was founded in2005. we are the only one company in China who just focus on EVA film business. " Professional, High quality, High-Tech" is our spirits.

 

E&N company have the best workshop in China who equipped three automatic EVA film production machines and all of the workshops are all 10000 class purified dust-free clean room. Thickness computer control and constant temp. and humitiy control make sure each roll EVA film is good and stable quality.

 

 

Quality Control

 

E&N Company follow up our products quality from procurement raw material to final product inspection. we have our own laboratory and full set of test machines to test every batch of production before delivery.

 
 

Hot Products

Advanges: 1.Superior stability after breakage and High fracture integrity. 2.Cross-linking :85-95% ...
Advanges: 1.Superior stability after breakage and High fracture integrity. 2.Cross-linking :85-95% ...
Advanges: 1.Superior stability after breakage and High fracture integrity. 2.Cross-linking :85-95% ...
Advanges: 1.Superior stability after breakage and High fracture integrity. 2.Cross-linking :85-95% ...
Advantage 1.Superior stability after breakage and High fracture integrity. 2.Cross-linking :85-95% ...
Advantage 1.Superior stability after breakage and High fracture integrity. 2.Cross-linking :85-95% ...