Special color electrophoresis paint for fire equipment
HS-6060LB Color Epoxy acrylic Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd.
|
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal such as: cold and hot rolled steel sheet, aluminum products, and stainless steel sheet etc. It is widely used in the electrophoresis coating of spring, hardware, home appliance, stationery, auto parts, electric car, groove pipe fittings etc
|
The appearance of the coating is flat, delicate, smooth, uniform high gloss
| Good stability of bath can adaptable for a longer updating cycle |
The bath has strong anti-shrinkage and anti-pollution ability
| Coating fullness of good, better substrate hiding |
1,Curing agent: totally enclosed multi-isocyanates
2,Solvent: alcohol ether
3,Pigment: Titanium pigment, Organic pigment, kaolin, antirust
pigment
Product quality data
| Project | Technical data | Test standard | ||
| Resin (HS-6060LB) | Color Paste | |||
| pH | 25℃ | 6.0±1.0 | —— | GB/T 9724 |
| Conductivity | 25℃, μs/cm | 1300±400 | —— | HG/T 3334 |
| Appearance | —— | Milky white liquid | viscous liquid,no agglomeration | Visual |
| Storage stability | No stratified state, and there were no obvious difference compared to before storage | In 5-35 ℃ temperature 1 year | ||
Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution
Filling tank proportion and method :
⑴ Bath preparation
Ratio:
Resin 750.00-1000.00
Paste 250.00
DI water 1900.00-2200.00
Total 3025.00-3575.00
⑵ Ripening conditions
Sample quantity: 3000～4000g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 28-34℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(180-185)℃×(20-30)min (Keeping temperature of parts coated)
Storage, packaging and transportation :
This product is a water-borne industrial coatings, non-hazardous, non-inflammable and explosive products; transportation to prevent direct sunlight, avoid freezing (>5℃ ); Packaging for 50/60/200L Plastic barrel; in the transport and storage of drums should be maintained clean, avoid charging the dirt brought in on drums during filling tank, again checked and confirmed that the quality of products, including paste resin, emulsions and additives should be indoor storage, good ventilation, dry, protect against freezing and overheating, the storage temperature should be controlled at 5～35℃, products from the date of production, over shelf, experimentation is required to determine whether can continue to use.