Low temperature curing electrophoresis paint for auto parts
Product Introduction :
OHT-825/OHT-825 Ultra Low temperature Black Cationic Epoxy Electrocoat, is HLS Paint (Shanghai) Co., Ltd. the ninth generation of independent research and development of electrophoretic coating. The lead, cadmium, chromium, mercury and other heavy metals, two-component aqueous dispersion resin. At the same time, inherited the characteristics of several generations of product quality, OHT-825 on galvanized steel sheet has good adaptability, almost at the bottom of all the metal material coating
such as: cold rolled steel, galvanized steel, aluminum, stainless steel plate, rubber parts, zinc and aluminum alloy plate, such as applicable.
This product features shown below:
Good stability of bath can adaptable for a longer updating cycle.
|
The bath has strong anti-shrinkage and anti-pollution ability. |
High penetration and good uniformity of internal and external.
|
Particularly suitable for high temperature baking of the workpiece, in particular, rubber and metal binding parts and zinc aluminum alloy material.
|
Main ingredients:
Curing agent: Modified low temperature curing agent
| Neutralizing agent: organic acid |
Solvent: alcohol ether
| Pigment: carbon black, kaolin, antirust pigment |
Product film performance :
| Project | Indicator | Test standard | |
| Appearance | Normal / Abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm,≥ | 7 | GB/T 9753 |
| Adhesion | level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | Kg.cm | 50 | GB/T 1732 |
| Gloss | 60° | 60-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃ ≥ | 240 | GB/T 1733 |
| Acid resistance | h(0.05N H2SO4) ≥ | 48 | GB/T 9274 |
| Alkali resistance | h(0.1N NaOH) ≥ | 48 | GB/T 9274 |
| *Salt spray resistance | film thickness ≥ 20μm | 800 | JIS K 5600-7-1 |
* Note: The substrate use the Bonder standard phosphating steel
panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Specification statement :
This manual contains information and recommendations are based on our current knowledge and experience, accurate to the date of publication so far. It cannot be used as a guarantee or commitment, in any case, responsibility for users to decide on the use of this product is intended availability. We remain in the process or new development within the scope of the right to change product specifications. Because we cannot control the construction conditions, hope through customers own experiments to determine satisfaction with the final results.