Sichuan Chang Yang Composites Company Limited |
|
S-Glass Roving (High Strength Glass Fiber)
CYC S-Glass Roving (HS2, HS4, HS6) is made from magnesium-alumina-silicate glass system. Foreign countries named as R-glass or T-glass. Due to its high tensile strength, high tensile modulus, excellent impact resistance, aging & corrosion resistance properties, S-Glass fiber is designed for high performance composites industries specially, such as military, aerospace, defense, marine & shipbuilding, civil industry, sports and recreation industry worlwide.
PRODUCT FEATURES:
High tensile strength
High tensile modulus
Compatible with Epoxy, Phenolic & Vinly ester resin
Excellent aging & corrosion resistance
S-GLASS FIBER PROPERTIES:
Physics Properties | HS2 | HS4 | HS6 |
Original Fiber Tensile Strength (MPa) | ≥4100 (590KSI) | ≥4600 (660KSI) | ≥4800 (690KSI) |
Epoxy Wet Fiber Tensile Strength (MPa) | 3000~3400 (435~490KSI) | 3200~3600 (460~520KSI) | 3600~4000 (520~580KSI) |
Tensile Modulus (GPa) | 87~91 | 90~94 | 92~96 |
Elongation at Break (%) | 5.3 | 5.3 | 5.7 |
Softening Point (℃) | 910 | 940 | 960 |
TYPICAL PRODUCT SPECIFICATIONS:
Product Code | Filament Diameter (μm) | Linear Density (tex) | Tensile Strength (MPa) | Moisture Content (%) | Loss On Ignition (%) | Compatible Resin |
SCY11-HS2-240 | 11 | 240 | ≥3000 | ≤0.20 | 0.50~1.10 | EP/VE/PE |
SCY11-HS4-240 | 11 | 240 | ≥3200 | ≤0.20 | 0.50~1.10 | |
SCY11-HS6-240 | 11 | 240 | ≥3600 | ≤0.20 | 0.50~1.10 | |
SCY11-HS2-660 | 11 | 660 | ≥3000 | ≤0.20 | 0.50~1.10 | |
SCY11-HS4-660 | 11 | 660 | ≥3200 | ≤0.20 | 0.50~1.10 | |
SCY11-HS6-660 | 11 | 660 | ≥3600 | ≤0.20 | 0.50~1.10 | |
SCY17-HS2-2400 | 17 | 2400 | ≥3000 | ≤0.20 | 0.50~1.10 |
Notes: Customized specification is available.
PACKAGING:
CYC S-Glass Roving packed by standard exporting carbon boxes and pallets.
STORAGE:
Unless otherwise specified, CYC S-Glass roving should be stacked in dry and cool place with its original package, do not open the package cause damp.