ER3103 Aluminium Manganese Alloy Welding Wire

Description: ER3103 is aluminum alloy welding wire containing about 1% manganese. Characteristic: Besides the excellent welding performance,fine and bright welding appearance, this wire also has the features of corrosion resistance,high strength(comparing with pure aluminium), good weldability...
Send Inquiry

Description

Description:ER3103 is aluminum alloy welding wire containing about 1% manganese.

Characteristic:Besides the excellent welding performance,fine and bright welding appearance, this wire also has the features of corrosion resistance,high strength(comparing with pure aluminium), good weldability and plasticity. After the anodization treatment, the color is in good matching.

Application: Applying for argon arc welding of 3XXX series alumal, and as filling materials of gas shielded welding.

Chemical composition(%)

Element

Si

Fe

Cu

Mn

Mg

Cr

Zn

Ti+Zr

Al

Be

others

GB/T Standard

0.50

0.70

0.10

0.9-1.5

0.3

0.1

0.2

0.1

margin

0.0003

single≤0.05 total≤0.15

Sample test value

0.05

0.12

0.04

1.12

0.006

0.005

0.002

0.008

margin

0.0001

/

Mechanical property of deposited metal(as welded)

Tensile Strength Rm/MPa

Yield strength Rel/p0.2 MPa

A (%) Percentages elongation after fracture A (%)

Shield gas

135

85

25

100%Ar

Welding Method:MIG


Physical properties of deposited metal

The range of melting temperature

Density(g/mm

643-654

2.7

Dry elongation: 15-25mm

Shield gas: 99.99%Ar, 75%Ar+25%He, 50%Ar+50%He

Welding reference parameters( Current polarity:MIG:DCTIG:AC)

MIG

Welding wire diameter(mm)

1.2

1.6

2.0

Welding current(A)

180-300

200-400

240-450

Welding voltage(V)

18-26

20-28

22-32

TIG

Welding wire diameter(mm)

1.6-2.5

2.5-4.0

4.0-5.0

Welding current(A)

150-250

200-320

220-400

Attention

Please remove the oxide film and grease of edge-weld and surface of welding wire from the welding parts Strictly , or it will form lack of fusion on welding line and cause blow hole, slag inclusion and such other defects.

To keep weld penetration without collapsing,please hold the melt metals by cushioning when weld the wire.

Website: www.sdkingdomcheer.com

Email: dora@kingdomcheer.com

Hot Tags: ER3103 aluminium manganese alloy welding wire, China, manufacturers, suppliers, wholesale

Related Products

  • C5 Hydrogenation Hydrocarbon Petroleum Resin

  • Isolated Soy Soya Protein Powder

  • Organic Chlorella Powder Tablet

  • LiFePo4 Lithium Polymer Battery

  • Battery for Consumer Electronics

  • Hydrochloric Acid

Feedback

Hot Products

Battery for Consumer Electronics Application: Main applications are lighting, toy, power bank, hand ...
ER5356 Alumina Magnesia Alloy Welding Wire Description: ER5356 is a kind of aluminium alloy welding ...
ER 1070 Aluminum Welding Wire Description: ER1070 is pure aluminium, Al content ≥99.7%. Characterist...
ER 1100 Aluminum Welding Wire Description: ER1100 is pure aluminium, Al content ≥99.0% Characteristi...
ER3103 Aluminium Manganese Alloy Welding Wire Description: ER3103 is aluminum alloy welding wire ...
ER4043 Aluminium Silicon Alloy Welding Wire Description: ER 4043 is aluminium-silicon alloy welding ...