Glass Seal 52 Nickel Iron Alloy Bar / Strip For Hermetic And Electronic Tube

Country/Region china
City & Province jiangsu
Categories Tinplate

Product Details

Glass Seal 52 Nickel Iron Alloy Bar / Strip For Hermetic And Electronic Tube

 

 

 

1  EQUIVALENT DESIGNATION

UNS N14052, Glass seal 52, Nilo® alloy 50, Pernifer 50

 

 

2 PRODUCT

Nickel iron alloy 52 (UNS N14052, Glass seal 52) bar, tube, strip, foil, wire for hermetic and electronic tube.

Alloy 52 is available in following standard semi-finished forms:

Sheet & plate

Delivery condition: Hot or cold rolled, heat treated, descaled or pickled

Strip & foil

Delivery condition: Cold rolled, heat treated, pickled or bright annealed

Bar and rod

Delivery condition: Forged, rolled, drawn, heat treated, oxidized, descaled or pickled, turned, peeled, ground or polished

Wire (profile, round, flats, square)

Delivery condition: Drawn bright, ¼ hard to hard, bright annealed in rings, containers, on spools and headstocks

Wire rod

Delivery condition: hot rolled (dia.5.5mm to 40mm)

Others

Other shapes and dimensions such as discs, rings, seamless pipes and forgings can be requested.

 

3 OVERVIEW

Alloy 52 is a binary nickel-iron controlled expansion alloy containing 50.5% nickel, used in both for its controlled expansion characteristics as well as it’s magnetic shielding capabilities. It is an alloy developed for glass-to-metal seals for some of the soft glasses and some ceramics. It exhibits low thermal expansion properties. Due to a higher content of Nickel than its other Nickel Iron family members, it also exhibits good magnetic properties.The alloy’s rate of thermal expansion is virtually constant to a temperature of about 1050°F (565°C).

With the addition of Iron, Alloy 52 is more durable than Nickel by itself and exhibits good machining properties.

 

4 APPLICATION

Alloy 52 is commonly used in the semiconductor and telecommunications industry, mainly used for metal to glass, and ceramic to glass sealing for electronic tubes, automotive and industrial lamps, and specialty hermetic devices, mercury-wetted reed switches, magnetic reed switches and seals that need controlled linear expansion to approximately 977°F (525°C).

 

5 CHEMICAL COMPOSITION (wt%):

NiFeAlCoMnSiCPSCr
50.5Balance≤0.10≤0.50≤0.60≤0.30≤0.05≤0.025≤0.025≤0.25

 

6 PHYSICAL PROPERTY

Densitylb/cu in0.30
Specific Gravityg/cm38.30
Curie Temp°F986
°C530
Melting Point°F2600
°C1427
Electrical ResistivityMicro-ohm-cm44
ohm-cir mil/ft258
Thermal ConductivityW/cm °C0.14
BTU-in/sq. ft-hr-97
Specific HeatCal/g- °C0.12
BTU/lbm- °F0.12
Thermal Expansionppm / °F (75°F to 842°F)5.5
ppm / °C (25°C to 450°F)9.9
Modules of ElasticityMpsi23
kMPa159

 

Linear coefficient of thermal expansion

Degree CCoefficientDegree CCoefficient
30-10010.530-4509.6 - 10.7
30-15010.530-47510.1
30-20010.430-50010
30-25010.430-52510.4
30-30010.230-55010.2 - 10.7
30-325--30-60010.8
30-35010.230-70011.7
30-375--30-80012.5
30-40010.130-90013.3
30-425--30-100014.2

 

7 MECHANICAL PROPERTIES

Typical mechanical properties of Alloy 52 in annealed condition

Tensile strengthksi80
MPa552
Yield strengthksi40
MPa276
Elongation% in 2 in.35
Typical hardnessRockwell HRB80

 

8 WORKING INSTRUCTION

Alloys 52 can be hot or cold worked, machined and formed by processes similar to those used for austenitic stainless steels.

Heat treatment

Although the nickel-iron low expansion alloys are not hardenable, annealing and stress relief thermal treatments are at times necessary to promote structure uniformity and dimensional stability. The relief of stresses introduced by severe forming, bending, or machining, can be accomplished by annealing at temperatures of approximately 1400 to 1800°F (760 to 982°C) for a time sufficient, to thoroughly heat through the section. However, the nickel-irons will oxidize readily at these high temperatures. When annealing cannot be done in a non-oxidizing enviroment (vacuum, dry hydrogen, dissociated ammonia, etc.) sufficient material must be allowed on work pieces to clean-up by light grinding, pickling, etc., after annealing. Stress relief for sections having light finishing cuts or grinding performed after annealing is accomplished by heating to 600 to 800°F (316 to 427°C), for a time to uniformly heat through the work piece.

Forming

All of the nickel-iron controlled expansion alloys can be hot forged, upset, formed, etc., at temperatures between 1800 to 2100°F (982 to 1149°C). However, heating for hot working must be done uniformly at slow rates from relatively cold furnaces (black) to minimize the potential for cracking through large sections as a result of differential thermal expansion stresses. Large forgings should be annealed to promote uniformity after hot working.

Machining

The alloy should be machined in the annealed condition, using high speed steel or tungsten carbide tipped tools. Cutting compounds should be straight cutting oil E.P. medium duty, or soluble oil 20:1 dilution for turning, drilling and milling. Lower dilution ratios should be used for other machining methods.

The following feeds and speeds can be used as a general guide:

 Cutting SpeedFeed
Rough turning
depth of cut
1.25-2.5 mm
(0.05-0.10 inch)
30-45 m/min
(98-148 ft/min)
0.25-0.4 mm/rev
(0.01-0.015 in/rev)
Finish turning,
depth of cut
0.125-0.25 mm
(0.005-0.010 inch)
45-60 m/min
(148-197ft/min)
0.1-0.25 mm/rev
(0.0004-0.01 mm/rev)

 

9 STANDARD SPECIFICATION

ASTM F-30 Sheet, strip, rod, bar, tubing and wire

MIL 1-23011 Class 2

AMS 1-23011 Class 2

 

10 COMPETITIVE ADVANTAGE:

(1) More than 50 years experience of research and develop in high temperature alloy, corrosion resistance alloy, precision alloy, refractory alloy, rare metal and precious metal material and products.
(2) 6 state key laboratories and calibration center.
(3) Patented technologies.

(4) Ultra-purity smelting process: VIM + IG-ESR + VAR

(5) Excellent high performance.

 

11 BUSINESS TERM

Minimum order quantityNegotiable
PriceNegotiable
Packing detailsWater prevent, seaworthy transport, mill’s export standard packing
MarkAs per order
Delivery time60-90 days
Payment termsT/T, L/C at sight, D/P
Supply ability300 metric tons / Month

 

Hot Products

Alloy 105, Nimonic® alloy 105 for ultra-supercritical thermal turbine blade, forgings, ring, ...
1 PRODUCT World first calss quality stainless steel AISI 440C (UNS S44004) bright bar for high end ...
1 PRODUCT Wear resistant copper alloy is a kind of wear-resistant alloy based on copper, which can ...
Precision Cobalt Alloy PRECISION ALLOYS Stamping Mold Conical Punch 1 PRODUCT Shape memory alloys ...
300M High Strength Steel Special Alloys For Aerospace And Defense With Good Ductility 1 PRODUCT ...
Product Description: Special Alloys For Aerospace And Defense offer a unique combination of superior ...