Hard Chrome Rod Micro Alloy Steel With Superior Turning Performance
Product Description
1. Low processing cost, needless quenched and tempered process and
the second turning.
2. Shortened processing periods, enhance productivity and reduce
the occupied capital.
3. Stable and uniform mechanical properties
4. Energy conservation: Production no quenched and tempered process
greatly saves the energy
consumption.
5. Environments protection: Production no quenched and tempered
process meets the requirements of
environmental protection.
6. It can be used for manufacturing injuection molding machine
draglink, engineering machinery push
rod and hydraulic prop with the feature that
hardened and tempered steel mechanical property
needless quenched and tempered process.
Detailed Description
1. MATERIAL: HY4700, HY4520
2. CHEMICAL COMPOSITION(%)
Material | C% | Mn% | Si% | S% | P% | V% | Ni | Cr% | Mo | Cu |
HY4700 | 0.38-0.45 | 1.20 ~1.60 | 0.30~0.50 | ≤0.035 | ≤0.020 | 0.05～0.15 | ≤0.25 | 0.10～0.20 | ≤0.15 | 0.25 |
HY4520 | 0.40 ~0.48 | 0.80 ~1.40 | 0.15 ~0.35 | ≤0.035 | ≤0.035 | ≤0.15 | ≤0.25 | ≤0.25 | ≤0.15 | ≤0.25 |
3. MECHANICAL PROPERTIES
Material | MECHANICAL PROPERTIES | Surface hardness(HBW) | |||||
Rm(MPa) | Rel(MPa) | A% | Z% | KU2(J) |
| ||
HY4700 | Φ35 - Φ100 | 900 - 1100 | ≥650 | ≥16 | ≥35 | ≥39 | 270-340 |
＞Φ100 - Φ140 | 850 - 950 | ≥600 | ≥16 | ≥35 | ≥39 | 270-340 | |
HY4520 | Φ40 - Φ100 | 750 - 900 | ≥520 | ≥19 | ≥40 | ≥39 | 230-290 |
＞Φ100～Φ140 | 750 - 900 | ≥520 | ≥17 | ≥35 | ≥39 | 230-290 | |
|
|
|
|
|
|
|
|
4. SUPPLY CONDITION
Ground and chrome plated
5. CHROME THICKNESS
20 to 30 micron
6. TOLERANCES ON DIA
ISO f7 on the diameter
7.OVALITY
Half of the tolerance ISO f7
8. STRAIGHTNESS
≤0.2MM/M
9. SURFACE ROUGHNESS
Ra≤0.2 micron and Rt≤2 micron
10 .SURFACE HARDNESS
850-1150HV (vickers 100g)
11. COHESION
No craks,breaking or detaching after thermic shock(warming up at 300 celsius degrees
and cooling in water)
12. CORROSION RESISTANCE
Test in natural salt spray according to ASTM B 117-120hours
Results evaluation according to ISO 4540 RATING 7-10
13. WELDABILITY
Good
14.POROSITY
Test according to ISO 1456/1458 and result yaluation according to ISO 4540 rating 8-10
15. PACKING
Anti rust oil to be applied on material and each rod to be packed in paper sleeve
16. CERTIFICATE
All certificate related with material heat treatment and plating is required