Alumina ceramic components / relay ceramic assemblies / ceramic - metal brazed contactor
1. Description:
1) ISO pressing --- ISO pressing is a forming process where our in house spray dried material is used to fill a mold and then compacted at around 20,000 PSI. ISO pressing is used to create blanks of certain sizes and shapes that cannot be easily formed by dry pressing or the extrusion process. These blanks can then be machined green or in the bisque state.
2) Bisque --- Bisque alumina is material that has been pressed or compacted into shape and then is partially fired. This enables the material to become harder than “green” material but not as hard as fully fired alumina. Bisque firing allows the material to be machined using conventional methods and tooling. Once bisqued, the material has a hard chalky feel to it. Bisque material can be used to create prototypes or one off parts. Once the part is complete, bisque alumina can be fully fired to achieve a harder, fully dense part with all the properties of alumina.
2. Feature Advantages:
1) High elasticity modulus
2) High compressive strength.
3) Anti corrosion
4) Abrasion resistance
5) Impact resistance
6) High precision
7) High stability
8) Good advanced ceramic materials
9) High welding sealing performance
10) High hardness and high density
11) Low thermal conductivity
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
16) High temperature resistance
17) A variety of specifications is available
18) Satisfy various technical requests
19) Lower medium spoilage
20) Stiffness texture
21) Widely apply for automotive ceramic sensor , ceramic heater ,electric heating
3. Material Features / Properties:
| Color | White or Ivory | White or Ivory | White or Ivory | |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics | ||||||||
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | Pass | - | |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | Pass | Pass | Pass | - | - | - | |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | ≤8 | - | |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - | |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | - | 4 | ||
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - | |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ | ||||||||
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - | |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - | |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - | ||
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - | ||
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - | |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Inspecting --- Packing
6. Application Fields:
New energy vehicles, charging piles, solar power generation, energy storage and power storage system, electric vehicle power system and so on.
7. Production Facilities: Prilling Tower , Forming Machine , High Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer , Granulometer , Helium Mass Spectrometer Leak Detector , Universal Pull Force Meter
9. Order Flow Steps as belows: Inquiry ---Quotation --- Place an order --- Production --- Delivery
10. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ; Good Service
11. Shipping and Package:
12. Our aimed market:
Notes:Above information only for reference and please contact with us for more details freely when you have any inquiry!