1. Description:
Table 11 lists some typical permanent-magnet materials. The alnicos are brittle and hence can be used only in cast or sintered form. The hexagonal ferrites are oxides having the general formula MO·6Fe2O3, where M is barium or strontium. The magnets are prepared by ceramic techniques and are often called ceramic magnets. Large numbers of low-cost ferrite magnets are bonded in plastics and widely used in door catches, wall magnets, refrigerator door gaskets, and toys.
2. Feature Advantages:
1) High elasticity modulus
2) High compressive strength.
3) Anti corrosion
4) Abrasion resistance
5) Impact resistance
6) High precision
7) High stability
8) Good advanced ceramic materials
9) High welding sealing performance
10) High hardness and high density
11) Low thermal conductivity
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
16) High temperature resistance
3. Material Features / Properties:
| Color | White or Ivory | White or Ivory | White or Ivory | |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics | ||||||||
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | Pass | - | |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | Pass | Pass | Pass | - | - | - | |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | ≤8 | - | |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - | |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | - | 4 | ||
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - | |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ | ||||||||
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - | |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - | |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - | ||
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - | ||
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - | |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Inspecting --- Packing
6. Application Fields:
Microwave Magnetron Ceramic for Home Electrical Appliances , Aerospace and Other Industry!
7. Production Facilities: Prilling Tower , Forming Machine , High Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer , Granulometer , Helium Mass Spectrometer Leak Detector , Universal Pull Force Meter
9. Notes:Above information only for reference and please contact with us for more details freely when you have any inquiry!